Diamond ASA S170
Acrylonitrile Styrene Acrylate
Product Description:
Diamond ASA S170 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in North America. Characteristics include:
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Agency Ratings
|
|
|
RoHS Compliance
|
|
|
Forms
|
|
|
Processing Method
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
|||
|
--
|
1.06
|
g/cm3
|
ASTM D792 |
|
23°C
|
1.06
|
g/cm3
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ASTM D1238,ISO 1133 | ||
|
220°C/10.0 kg
|
12
|
g/10 min
|
|
|
230°C/3.8 kg
|
2.4
|
g/10 min
|
|
|
Molding Shrinkage - Flow
|
0.40 to 0.80
|
%
|
ASTM D955 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
|||
|
R-Scale, Injection Molded
|
91
|
ASTM D785 | |
|
R-Scale, 23°C
|
95
|
ISO 2039-2 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength - Flow
|
|||
|
Yield, 23°C, Injection Molded2
|
40.9
|
MPa
|
ASTM D638 |
|
Yield, Injection Molded
|
39.8
|
MPa
|
ISO 527-2/50 |
|
Flexural Modulus - Chord, Flow
|
|||
|
23°C, Injection Molded
|
2010
|
MPa
|
ASTM D790 |
|
23°C, Injection Molded
|
2050
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | ||
|
-30°C, Injection Molded
|
10
|
kJ/m2
|
|
|
23°C, Injection Molded
|
25
|
kJ/m2
|
|
|
Notched Izod Impact
|
|||
|
Flow : -30°C, Injection Molded
|
130
|
J/m
|
ASTM D256 |
|
Flow : 23°C, Injection Molded
|
400
|
J/m
|
ASTM D256 |
|
-30°C, Injection Molded
|
8.3
|
kJ/m2
|
ISO 180 |
|
23°C, Injection Molded
|
31
|
kJ/m2
|
ISO 180 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 3.18 mm, Injection Molded
|
88.6
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed
|
88.5
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed, 3.18 mm, Injection Molded
|
75.7
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed
|
75.3
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
102
|
°C
|
ASTM D1525,ISO 306 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : -30 to 80°C
|
8.4E-5
|
cm/cm/°C
|
|
|
Transverse : -30 to 80°C
|
1.0E-4
|
cm/cm/°C
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80 to 85
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.10
|
%
|
|
|
Suggested Shot Size
|
40 to 70
|
%
|
|
|
Suggested Max Regrind
|
30
|
%
|
|
|
Rear Temperature
|
230 to 260
|
°C
|
|
|
Middle Temperature
|
232 to 265
|
°C
|
|
|
Front Temperature
|
235 to 272
|
°C
|
|
|
Nozzle Temperature
|
220 to 272
|
°C
|
|
|
Processing (Melt) Temp
|
220 to 272
|
°C
|
|
|
Mold Temperature
|
40 to 80
|
°C
|
|
|
Injection Rate
|
Fast
|
||
|
Back Pressure
|
0.517 to 1.03
|
MPa
|