Luran? S 776S
Acrylonitrile Styrene Acrylate
Product Description:
Luran? S 776S is suitable for injection molding applications. It provides good impact toughness and enables matte surface appearance for extruded sheets. FEATURES APPLICATIONS
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
UL Yellow Card2
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Uses
|
|
|
Forms
|
|
|
Processing Method
|
|
|
Multi-Point Data
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.07
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
4.0
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage3
|
0.40 to 0.70
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
1.7
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.35
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
70.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
2200
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Yield, 23°C)
|
47.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Yield, 23°C)
|
3.3
|
%
|
ISO 527-2 |
|
Nominal Tensile Strain at Break (23°C)
|
12
|
%
|
ISO 527-2 |
|
Tensile Creep Modulus (1000 hr)
|
1200
|
MPa
|
ISO 899-1 |
|
Flexural Stress (23°C)
|
65.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
4.0
|
kJ/m2
|
|
|
23°C
|
30
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature4
|
|||
|
0.45 MPa, Annealed
|
101
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Annealed
|
96.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
92.0
|
°C
|
ISO 306/B50 |
|
--
|
104
|
°C
|
ISO 306/A50 |
|
CLTE - Flow
|
8.0E-5 to 1.1E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.17
|
W/m/K
|
DIN 52612 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E 13
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
1.0E 14
|
ohms·cm
|
IEC 60093 |
|
Relative Permittivity
|
IEC 60250 | ||
|
100 Hz
|
3.80
|
||
|
1 MHz
|
3.40
|
||
|
Dissipation Factor
|
IEC 60250 | ||
|
100 Hz
|
9.0E-3
|
||
|
1 MHz
|
0.034
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Processing (Melt) Temp
|
240 to 280
|
°C
|
|
|
Mold Temperature
|
40 to 80
|
°C
|
| Notes |