东莞市裕升高分子材料有限公司
GELOY? Resin XP7560 - Asia
Acrylonitrile Styrene Acrylate
Product Description:
PC/ASA. Excellent weatherability.
| General | |
|
Material Status
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Uses
|
|
|
Appearance
|
|
|
Processing Method
|
|
|
Also Available In
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.10
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
|
20
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage - Flow1
|
0.40 to 0.60
|
%
|
Internal Method |
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.80
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.30
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
111
|
ISO 2039-2 | |
|
Ball Indentation Hardness (H 358/30)
|
92.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
2460
|
MPa
|
ISO 527-2/1 |
|
Tensile Stress
|
ISO 527-2/50 | ||
|
Yield
|
55.0
|
MPa
|
|
|
Break
|
43.0
|
MPa
|
|
|
Tensile Strain
|
ISO 527-2/50 | ||
|
Yield
|
3.7
|
%
|
|
|
Break
|
20
|
%
|
|
|
Flexural Modulus2
|
2500
|
MPa
|
ISO 178 |
|
Flexural Stress2,3
|
82.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength4
|
ISO 180/1A | ||
|
-30°C
|
8.0
|
kJ/m2
|
|
|
23°C
|
20
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature5
|
|||
|
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span
|
102
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span
|
86.0
|
°C
|
ISO 75-2/Ae |
|
Vicat Softening Temperature
|
|||
|
--
|
107
|
°C
|
ISO 306/B120 |
|
--
|
102
|
°C
|
ISO 306/B50 |
|
--
|
113
|
°C
|
ISO 306/A50 |
|
Ball Pressure Test
|
IEC 60695-10-2 | ||
|
73 to 77°C
|
Pass
|
||
|
95°C6
|
Pass
|
||
|
CLTE - Flow (23 to 60°C)
|
9.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.20
|
W/m/K
|
ISO 8302 |
| Flammability |
Nominal Value
|
Test Method
|
|
|
Flame Rating (3.2 mm, Testing by SABIC)
|
HB
|
UL 94 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
90 to 100
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.050
|
%
|
|
|
Hopper Temperature
|
60 to 80
|
°C
|
|
|
Rear Temperature
|
220 to 250
|
°C
|
|
|
Middle Temperature
|
230 to 260
|
°C
|
|
|
Front Temperature
|
240 to 270
|
°C
|
|
|
Nozzle Temperature
|
230 to 260
|
°C
|
|
|
Processing (Melt) Temp
|
250 to 270
|
°C
|
|
|
Mold Temperature
|
50 to 70
|
°C
|