RONFALIN? ASA 3422 U
Acrylonitrile Styrene Acrylate
Product Description:
High flow ASA grade with enhanced UV stability. (Former name: POLYMAN ASA E/MI 1010 UV)
| General | |
|
Material Status
|
|
|
Literature1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Features
|
|
|
Processing Method
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.08
|
g/cm3
|
ISO 1183/A |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
14
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
0.40 to 0.70
|
%
|
ISO 294-4 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness (H 358/30)
|
96.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
3000
|
MPa
|
ISO 527-2/1A/1 |
|
Tensile Stress
|
ISO 527-2/1A/50 | ||
|
Yield
|
50.0
|
MPa
|
|
|
Break
|
45.0
|
MPa
|
|
|
Tensile Strain (Yield)
|
3.5
|
%
|
ISO 527-2/1A/50 |
|
Nominal Tensile Strain at Break
|
5.0
|
%
|
ISO 527-2/1A/50 |
|
Flexural Modulus2
|
2600
|
MPa
|
ISO 178 |
|
Flexural Stress2 (4.8% Strain)
|
80.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
2.0
|
kJ/m2
|
|
|
23°C
|
8.0
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
90.0
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
100
|
°C
|
ISO 306/B50 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E 15
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
1.0E 13
|
ohms·m
|
IEC 62631-3-1 |
|
Comparative Tracking Index
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Burning Rate
|
|||
|
2.00 mm
|
100
|
mm/min
|
ISO 3795 |
|
2.00 mm
|
100
|
mm/min
|
FMVSS 302 |
|
Flammability Classification
|
IEC 60695-11-10, -20 | ||
|
1.5 mm
|
HB
|
||
|
3.0 mm
|
HB
|