Product Description:
Luran? S KR2863C is a blend of ASA and PC providing high impact strength and the highest heat resistance within the product line. FEATURES APPLICATIONS
General | |
Material Status
|
|
Literature1
|
|
Search for UL Yellow Card
|
|
Availability
|
|
Features
|
|
Forms
|
|
Processing Method
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.16
|
g/cm3
|
ISO 1183 |
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
|
18
|
cm3/10min
|
ISO 1133 |
Molding Shrinkage2
|
0.30 to 0.70
|
%
|
ISO 294-4 |
Water Absorption
|
ISO 62 | ||
Saturation, 23°C
|
0.60
|
%
|
|
Equilibrium, 23°C, 50% RH
|
0.16
|
%
|
|
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Ball Indentation Hardness
|
110
|
MPa
|
ISO 2039-1 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus
|
2500
|
MPa
|
ISO 527-2 |
Tensile Stress (Yield, 23°C)
|
62.0
|
MPa
|
ISO 527-2 |
Tensile Strain (Yield, 23°C)
|
4.9
|
%
|
ISO 527-2 |
Nominal Tensile Strain at Break (23°C)
|
50
|
%
|
ISO 527-2 |
Flexural Stress (23°C)
|
93.0
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179 | ||
-30°C
|
17
|
kJ/m2
|
|
23°C
|
60
|
kJ/m2
|
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Heat Deflection Temperature3
|
|||
0.45 MPa, Annealed
|
130
|
°C
|
ISO 75-2/B |
1.8 MPa, Annealed
|
109
|
°C
|
ISO 75-2/A |
Vicat Softening Temperature
|
|||
--
|
130
|
°C
|
ISO 306/B50 |
--
|
140
|
°C
|
ISO 306/A50 |
CLTE - Flow
|
7.0E-5 to 9.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
Thermal Conductivity
|
0.17
|
W/m/K
|
DIN 52612 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E 14
|
ohms
|
IEC 60093 |
Volume Resistivity
|
1.0E 15
|
ohms·cm
|
IEC 60093 |
Relative Permittivity
|
IEC 60250 | ||
100 Hz
|
3.10
|
||
1 MHz
|
3.00
|
||
Dissipation Factor
|
IEC 60250 | ||
100 Hz
|
6.0E-3
|
||
1 MHz
|
0.010
|