XENOY XL1562 is an impact modified PBT+PC blend with outstanding chemical resistance, good UV stability and flow properties.

Information provided by SABIC

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/in3	ISO 1183
Water Absorption	0.500 %	0.500 %	23°C/sat; ISO 62
Moisture Absorption	0.150 %	0.150 %	23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.00800 - 0.0110 cm/cm	0.00800 - 0.0110 in/in	SABIC method
Linear Mold Shrinkage, Transverse	0.00800 - 0.0110 cm/cm	0.00800 - 0.0110 in/in	SABIC method
Melt Flow	9.00 g/10 min @Load 2.16 kg, Temperature 250 °C	9.00 g/10 min @Load 4.76 lb, Temperature 482 °F	cm3/10 min; ISO 1133
	27.0 g/10 min @Load 5.00 kg, Temperature 250 °C	27.0 g/10 min @Load 11.0 lb, Temperature 482 °F	cm3/10 min; ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
Tensile Strength, Yield	54.0 MPa	7830 psi	50 mm/min; ISO 527
Elongation at Break	100 %	100 %	50 mm/min; ISO 527
Elongation at Yield	5.00 %	5.00 %	50 mm/min; ISO 527
Tensile Modulus	2.10 GPa	305 ksi	1mm/min; ISO 527
Flexural Yield Strength	74.0 MPa	10700 psi	2 mm/min; ISO 178

PC/PBT XENOY XL1562  

PC/PBT是塑料合金bai,它保持了结晶材du料PBT的耐化学性及zhi易于成型等特dao点，又兼备了非结zhuan晶材料PC的韧性和shu尺寸稳定性。其产品广泛应用于汽车保险杠、汽车拉手、电子元件等。 PC/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。

PC-PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应

PC-PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象

PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点

PC-PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间

抗高温变形对于大形的外壳类材料具有重要的意义。

PC/PBT是塑料合金,它保持了结晶材料PBT的耐化学性及易于成型等特点，又兼备了非结晶材料PC的韧性和尺寸稳定性。其产品广泛应用于汽车保险杠、汽车拉手、电子元件等。 PC/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。