TPEE KEYFLEX BT HB9242D 

Description: TPC-ET, Blow Moldable, Low Modulus, Black Color

Application: Cable & Wire Jackets, Hose & Tubing, Sheet

CAS: 37282-12-5 and 1333-86-4

Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Water Absorption	0.60 % @Temperature 23.0 °C, Time 86400 sec	0.60 % @Temperature 73.4 °F, Time 24.0 hour	ASTM D570
Maximum Moisture Content	0.010	0.010	Injection Molding
	0.010	0.010	Extrusion Molding
Melt Flow	2.0 g/10 min @Load 2.13 kg, Temperature 230 °C	2.0 g/10 min @Load 4.70 lb, Temperature 446 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Shore A	95	95	ASTM D2240
Hardness, Shore D	39	39	ASTM D2240
Tensile Strength at Break	29.4 MPa @Thickness 2.00 mm	4260 psi @Thickness 0.0787 in	50mm/min; ASTM D638

TPEE KEYFLEX BT HB9242D 

TPEE性能：

热性能

TPEE具有优异的耐热性能，硬度越高，耐热性越好；TPEE在110～140℃连续加热10h基本不失重，在160℃和180℃分别加热10h，失重仅为0.05%和0.1%，因而TPEE的使用温度非常高，短期使用温度更高，能适应汽车生产线上的烘漆温度(150～160℃)，并且它在高低温下机械性能损失小。TPEE在120℃以上使用，其拉伸强度远远高于TPU此外TPEE还具有出色的耐低温性能，TPEE脆点低于-70℃并且硬度越低，耐寒性越好，大部分TPEE可在-40℃下长期使用。

耐化学介质性

TPEE具有极佳的耐油性，在室温下能耐大多数极性液体化学介质(如酸、碱、胺二醇类化合物)，但对卤代烃(氟里昂除外)及酚类的作用却无能为力，其耐化学品的能力随其硬度的提高而提高。TPEE对大多数有机溶剂、燃料及气体的抗溶胀性能和抗渗透性能是好的，对燃油渗透性仅为氯丁胶、氯磺化聚乙烯、丁腈胶等耐油橡胶的1/3～1/300但TPEE耐热水性较差，添加聚碳酰亚胺稳定剂可以明显改善其抗水解性能。

耐老化性

TPEE在很多不同条件下，如在水雾、臭氧、室外大气老化等条件下，化学稳定性优良。象大多数弹性体一样，在紫外光作用下会发生降解，因此对于室外应用或制品受阳光照射的条件，配方中应添加紫外光防护助剂，其中包括炭黑和各种颜料或其它屏蔽材料;此外TPEE还具有不同程度的水解性。

TPEE应用

TPEE主要用于要求减震、耐冲击、耐曲挠、密封性和弹性、耐油、耐化学品并要求足够强度的领域。如：聚合物改性、汽车部件、耐高低温电线护套、液压软管、鞋材、传动皮带、旋转成型轮胎、挠性连轴节、消音齿轮、电梯滑道、化工设备管道阀件中的防腐耐磨耐高低温材料等。TPEE高性能的产品牌号有美国杜邦公司的TPEE 5526,5556，4056，4069等，广泛用于电线电缆以及密封件等。