PC PBT MAKROBLEND UT4045 G

(PC PBT)-blend, 20% Glass fiber reinforced, easy release, injection molding. Makroblend UT4045G offers a high stiffness, excellent chemical resistance, good flowability and exceptional dimensional stability.

As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in3	ISO 1183-1
Filler Content	20 %	20 %	Method A; b.o. ISO 3451-1
Moisture Absorption at Equilibrium	0.15 %	0.15 %	ISO 62
Water Absorption at Saturation	0.30 %	0.30 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	150x105x3 mm; 260 °C / MT 80 °C; 600 bar; b.o. ISO 2577
	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	b.o. ISO 2577
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	150x105x3 mm; 260 °C / MT 80 °C; 600 bar; b.o. ISO 2577
Melt Flow	42 g/10 min @Load 5.00 kg, Temperature 260 °C	42 g/10 min @Load 11.0 lb, Temperature 500 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	90.0 MPa	13100 psi	ISO 2039-1
Tensile Strength at Break	100 MPa	14500 psi	5 mm/min; ISO 527-1,-2
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ISO 527-1,-2

PC PBT MAKROBLEND UT4045 G

PC PBT是塑料合金bai,它保持了结晶材du料PBT的耐化学性及zhi易于成型等特dao点，又兼备了非结zhuan晶材料PC的韧性和shu尺寸稳定性。其产品广泛应用于汽车保险杠、汽车拉手、电子元件等。 PC/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。

PC-PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应

PC-PBT是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象

PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点

PC-PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间

抗高温变形对于大形的外壳类材料具有重要的意义。

PC PBT是塑料合金,它保持了结晶材料PBT的耐化学性及易于成型等特点，又兼备了非结晶材料PC的韧性和尺寸稳定性。其产品广泛应用于汽车保险杠、汽车拉手、电子元件等。 PC/PBT具有PC和PBT二者的综合特性，例如PC的高韧性和几何稳定性以及PBT的化学稳定性、热稳定性和润滑特性等。

PC PBT MAKROBLEND UT4045 G 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！