苏州耐特森塑胶原料有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | 23℃ | ASTM D-792 | 1.20 | |
| 模缩率 | 流动方向 | ASTM D-955 | 0.5-0.7 | % | |
| 吸水率 | 24时间 | ASTM D-570 | 0.15 | % | |
| 熔融指数 | ASTM D1238 | 2.5 | g/10min | ||
| 吸水率 | 23℃ | ASTM D570 | 0.35 | % | |
| 吸水率 | 100℃ | ASTM D570 | 0.58 | % | |
| 机械性能 | 缺口冲击强度 | 23 ℃ | ASTM D-256 | 747 | J/M |
| 弯曲强度 | 23 ℃ | ASTM D-790 | 93 | MPa | |
| 弯曲模量 | 23 ℃ | ASTM D-790 | 2340 | MPa | |
| 拉伸应力 | ASTM D-638 | 65 | MPa | ||
| 拉伸应变 | ASTM D-638 | 110 | % | ||
| Izod缺口冲击强度 | 73?H | ASTM D256 | 747 | J/M | |
| Izod无缺口冲击强度 | 73?H | ASTM D4812 | 3204 | J/M | |
| 洛氏硬度 | ASTM D785 | 118 | R | ||
| 洛氏硬度 | ASTM D785 | 70 | M | ||
| 电气性能 | 体积电阻 | 23 ℃ | ASTM D-257 | 1.0E 16 | Ω |
| 损耗因数 | 60Hz | ASTM D-150 | 0.0009 | ||
| 介电常数 | 60Hz | ASTM D-150 | 3.17 | ||
| 热性能 | 线膨胀系数 | -40 ℃-95 ℃ | ASTM E831 | 6.84E-0.5 | 1/ ℃ |
| 热变形温度 | 1.82MPa | ASTM D-648 | 132 | ℃ | |
| 维卡软化温度 | ASTM D1525 | 157 | ℃ | ||