余姚乘风塑化有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 流动系数 | 200℃, 5kg | ASTM D-1238 | 2.8 | g/10min |
| 比重 | 23℃ | ASTM D-792 | 1.19 | ||
| 机械性能 | 引张强度 | 1/8",6mm/min | ASTM D-638 | 395 | kg/cm2 |
| 5600 | lb/in2 | ||||
| 延伸率 | 1/8",6mm/min | ASTM D-638 | 30 | % | |
| 弯曲强度 | 1/4",2.8mm/min | ASTM D-790 | 620 | kg/cm2 | |
| 8800 | lb/in2 | ||||
| 弯曲弹性率 | 1/4",2.8mm/min | ASTM D-790 | 25000 | kg/cm2 | |
| 350000 | lb/in2 | ||||
| IZOD缺口冲击强度 | 1/4",23℃ | ASTM D-256 | 20 | kg-cm/cm | |
| 3.7 | ft-lb/in | ||||
| 1/8",23℃ | 24 | kg-cm/cm | |||
| 4.4 | ft-lb/in | ||||
| 硬度 | 1/2" | ASTM D-785 | 98 | R Scale | |
| 热性能 | 维卡软化点 | 1/8",50℃/hr | ASTM D-1525 | 104 | ℃ |
| ?H | |||||
| 热变形温度 | 85℃，8hr ,1/4",120℃/hr | ASTM D-648 | 96(85) | ℃ | |
| 205(185) | ?H | ||||
| 燃烧率 | 1.6mm | UL 94 | V-0 | ||
| 2.5mm | 5VB | ||||