余姚乘风塑化有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.950 | g/cm3 | |
| 熔体流动速率 | ASTM D-1238 | 0.05 | g/10min | ||
| 机械性能 | 拉力降伏强度 | ASTM D-638 | 260 | KG/cm2 | |
| 拉力冲击强度 | ASTM D-1822 | 800 | kg.cm/cm2 | ||
| 拉力断裂强度 | ASTM D-638 | 380 | KG/m3 | ||
| 硬度 | ASTM D-2240 | 65 | Shore D | ||
| 拉力断裂伸长率 | ASTM D-638 | 800 | % | ||
| IZOD缺口冲击强度 | ASTM D-256 | 22 | kg.cm/cm | ||
| 热性能 | 软化点 | ASTM D-1525 | 123 | ℃ | |
| 熔点 | FPC | 130 | ℃ | ||
| 脆化温度 | ASTM D-746 | ＜-70 | ℃ | ||
| 其它性能 | ESCR | ASTM D-1693 | ＞1000 | Hours | |