Ultramid? 8202 HS
聚酰胺6
产品说明：
Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose PA6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.
Applications
Ultramid 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.
| 基本信息 |
|
| 添加剂 |
|
| 特性 |
- 低粘度
- 均聚物
- 良好的强度
- 良好耐磨损性
- 耐化学性良好
- 热稳定性
- 韧性良好
- 通用
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
- Isothermal Stress vs. Strain (ISO 11403-1)
- Secant Modulus vs. Strain (ISO 11403-1)
- Shear Modulus vs. Temperature (ISO 11403-1)
- Viscosity vs. Shear Rate (ISO 11403-2)
|
| 物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 比重 |
1.13 |
-- |
g/cm3 |
ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) |
1.2 |
-- |
% |
|
| 吸水率 |
|
|
|
|
| 24 hr |
1.6 |
-- |
% |
ASTM D570 |
| 23°C, 24 hr |
1.6 |
-- |
% |
ISO 62 |
| 饱和 |
9.5 |
-- |
% |
ASTM D570 |
| 饱和, 23°C |
9.5 |
-- |
% |
ISO 62 |
| 平衡, 50% RH |
2.7 |
-- |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
2.7 |
-- |
% |
ISO 62 |
| 硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 洛氏硬度 (R 级) |
119 |
-- |
|
ASTM D785 |
| 机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
ISO 527-2 |
| 23°C |
2700 |
970 |
MPa |
ISO 527-2 |
| 80°C |
485 |
550 |
MPa |
ISO 527-2 |
| 121°C |
360 |
320 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
|
| 屈服, -40°C |
126 |
110 |
MPa |
ASTM D638, ISO 527-2 |
| 屈服, 23°C |
79.0 |
36.0 |
MPa |
ASTM D638 |
| 屈服, 80°C |
35.0 |
30.0 |
MPa |
ASTM D638, ISO 527-2 |
| 屈服, 121°C |
25.0 |
20.0 |
MPa |
ASTM D638, ISO 527-2 |
| 屈服, 23°C |
78.0 |
36.0 |
MPa |
ISO 527-2 |
| 断裂, 23°C |
75.0 |
60.0 |
MPa |
ASTM D638 |
| 伸长率 |
|
|
|
|
| 屈服, 23°C |
4.0 |
16 |
% |
ASTM D638, ISO 527-2 |
| 屈服, 80°C |
42 |
35 |
% |
ASTM D638 |
| 屈服, 121°C |
36 |
40 |
% |
ASTM D638 |
| 断裂, 23°C |
55 |
> 100 |
% |
ASTM D638 |
| 标称拉伸断裂应变 (23°C) |
25 |
> 50 |
% |
ISO 527-2 |
| 弯曲模量 |
|
|
|
|
| -40°C |
3010 |
3660 |
MPa |
ASTM D790 |
| 23°C |
2830 |
740 |
MPa |
ASTM D790 |
| 65°C |
500 |
-- |
MPa |
ASTM D790 |
| 90°C |
350 |
-- |
MPa |
ASTM D790 |
| 121°C |
305 |
-- |
MPa |
ASTM D790 |
| 23°C |
2400 |
770 |
MPa |
ISO 178 |
| 弯曲强度 |
|
|
|
|
| -40°C |
170 |
154 |
MPa |
ASTM D790 |
| 23°C |
108 |
35.0 |
MPa |
ASTM D790 |
| 65°C |
30.0 |
-- |
MPa |
ASTM D790 |
| 90°C |
20.0 |
-- |
MPa |
ASTM D790 |
| 121°C |
17.0 |
-- |
MPa |
ASTM D790 |
| 23°C |
85.0 |
25.0 |
MPa |
ISO 178 |
| 冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 (23°C) |
3.5 |
-- |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度 |
|
|
|
ISO 179 |
| -30°C |
51 |
-- |
kJ/m2 |
ISO 179 |
| 23°C |
无断裂 |
-- |
|
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
|
ASTM D256 |
| -40°C |
48 |
43 |
J/m |
ASTM D256 |
| 23°C |
58 J/m |
无断裂 |
|
ASTM D256 |
| Drop Impact Resistance (23°C) |
142 |
> 271 |
J |
内部方法 |
| 热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
|
| 0.45 MPa, 未退火 |
178 |
-- |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
65.0 |
-- |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
60.0 |
-- |
°C |
ISO 75-2/A |
| 熔融峰值温度 |
220 |
-- |
°C |
ASTM D3418, ISO 3146 |
| 线形热膨胀系数 - 流动 |
8.3E-5 |
-- |
cm/cm/°C |
ASTM E831 |
| RTI Elec |
|
|
|
UL 746 |
| 0.710 mm |
130 |
-- |
°C |
UL 746 |
| 1.50 mm |
130 |
-- |
°C |
UL 746 |
| 3.00 mm |
130 |
-- |
°C |
UL 746 |
| 6.00 mm |
130 |
-- |
°C |
UL 746 |
| RTI Imp |
|
|
|
UL 746 |
| 0.710 mm |
95.0 |
-- |
°C |
UL 746 |
| 1.50 mm |
105 |
-- |
°C |
UL 746 |
| 3.00 mm |
105 |
-- |
°C |
UL 746 |
| 6.00 mm |
105 |
-- |
°C |
UL 746 |
| RTI |
|
|
|
UL 746 |
| 0.710 mm |
95.0 |
-- |
°C |
UL 746 |
| 1.50 mm |
105 |
-- |
°C |
UL 746 |
| 3.00 mm |
105 |
-- |
°C |
UL 746 |
| 6.00 mm |
105 |
-- |
°C |
UL 746 |
| 电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 体积电阻率 |
|
|
|
|
| 1.50 mm |
> 1.0E+13 |
-- |
ohms·cm |
ASTM D257 |
| -- |
> 1.0E+13 |
-- |
ohms·cm |
IEC 60093 |
| 介电强度 |
|
|
|
|
| 1.50 mm 1 |
22 |
-- |
kV/mm |
ASTM D149 |
| -- |
37 |
-- |
kV/mm |
IEC 60243-1 |
| 漏电起痕指数 |
600 |
-- |
V |
IEC 60112 |
| 可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
|
UL 94 |
| 0.710 mm |
V-2 |
-- |
|
UL 94 |
| 1.50 mm |
V-2 |
-- |
|
UL 94 |
| 3.00 mm |
V-2 |
-- |
|
UL 94 |
| 6.00 mm |
V-2 |
-- |
|
UL 94 |
| 注射 |
干燥 |
单位制 |
|
| 干燥温度 |
80.0 |
°C |
|
| 干燥时间 |
2.0 到 4.0 |
hr |
|
| 建议的最大水分含量 |
0.15 |
% |
|
| 加工（熔体）温度 |
240 到 285 |
°C |
|
| 模具温度 |
65.0 到 80.0 |
°C |
|
| 注塑压力 |
3.50 到 12.5 |
MPa |
|
| 注射速度 |
快速 |
|
|