SABIC HDPE M864SE

高密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

产品说明：

SABIC? HDPE M864SE is an UV stabilized, high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applications where rigidity, toughness and warp resistance are required.

Typical applications.
SABIC? HDPE M864SE is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items.

This product is not intended for and must not be used in any pharmaceutical/medical applications.

   
   
    
    SABIC HDPE M864SE 物性表
   
   
   
   
    
    
     
     
      
      基本信息
      
      
     
     
     
     
      
      添加剂
      
      
       
       
        
        紫外线稳定剂
       
       
     
     
     
     
      
      特性
      
      
       
       
        
        高密度
        
        抗弯曲
        
        抗紫外线性能良好
        
        韧性良好
        
        窄分子量分布
        
        中等硬度
       
       
     
     
     
     
      
      用途
      
      
       
       
        
        工业应用
        
        桶
        
        装货箱
       
       
     
     
     
     
      
      加工方法
      
      
       
       
        
        注射成型
       
       
     
     
    
    
   
   
   
   
    
    
     
     
      
      物理性能
      
      额定值
      
      单位制
      
      测试方法
     
     
     
     
      
      密度
      
      0.964
      
      g/cm3
      
      ISO 1183
     
     
     
     
      
      熔流率（熔体流动速率）
      
      
      
      
      
      ISO 1133
     
     
     
     
      
          190°C/2.16 kg
      
      8.0
      
      g/10 min
      
      ISO 1133
     
     
     
     
      
          190°C/5.0 kg
      
      22
      
      g/10 min
      
      ISO 1133
     
     
     
     
      
      抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型)
      
      90.0
      
      hr
      
      内部方法
     
     
    
    
   
   
   
   
    
    
     
     
      
      硬度
      
      额定值
      
      单位制
      
      测试方法
     
     
     
     
      
      肖氏硬度 (邵氏 D, 模压成型)
      
      65
      
      
      
      ISO 868
     
     
    
    
   
   
   
   
    
    
     
     
      
      机械性能
      
      额定值
      
      单位制
      
      测试方法
     
     
     
     
      
      拉伸模量 (2.00 mm, 模压成型)
      
      1450
      
      MPa
      
      ISO 527-2/1BA/50
     
     
     
     
      
      拉伸应力
      
      
      
      
      
      ISO 527-2/1BA/50
     
     
     
     
      
          屈服, 2.00 mm, 模压成型
      
      32.0
      
      MPa
      
      ISO 527-2/1BA/50
     
     
     
     
      
          断裂, 2.00 mm, 模压成型
      
      15.0
      
      MPa
      
      ISO 527-2/1BA/50
     
     
     
     
      
      拉伸应变 (断裂, 2.00 mm, 模压成型)
      
      > 200
      
      %
      
      ISO 527-2/1BA/50
     
     
     
     
      
      弯曲模量 (2.00 mm, 模压成型)
      
      1700
      
      MPa
      
      ISO 178
     
     
     
     
      
      弯曲应力 (2.00 mm, 模压成型)
      
      32.0
      
      MPa
      
      ISO 178
     
     
    
    
   
   
   
   
    
    
     
     
      
      冲击性能
      
      额定值
      
      单位制
      
      测试方法
     
     
     
     
      
      悬壁梁缺口冲击强度 (23°C, 模压成型)
      
      4.0
      
      kJ/m2
      
      ISO 180/A
     
     
    
    
   
   
   
   
    
    
     
     
      
      热性能
      
      额定值
      
      单位制
      
      测试方法
     
     
     
     
      
      热变形温度 (0.45 MPa, 未退火)
      
      95.0
      
      °C
      
      ISO 75-2/B
     
     
     
     
      
      维卡软化温度
      
      129
      
      °C
      
      ISO 306/A
     
     
     
     
      
      溶融温度（DSC）
      
      135
      
      °C
      
      ISO 11357-3
     
     
     
     
      
      Enthalpy Change
      
      229
      
      J/g
      
      ISO 11357-3
     
     
    
    
   
   
   
   
    
    
     
     
      
      注射
      
      额定值
      
      单位制
      
      
     
     
     
     
      
      加工（熔体）温度
      
      230 到 275
      
      °C
      
      
     
     
     
     
      
      模具温度
      
      32.0 到 38.0
      
      °C
      
      
     
     
     
     
      
      注塑压力
      
      69.0 到 89.0
      
      MPa

基本信息
添加剂	紫外线稳定剂
特性	高密度抗弯曲抗紫外线性能良好韧性良好窄分子量分布中等硬度
用途	工业应用桶装货箱
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度	0.964	g/cm3	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	8.0	g/10 min	ISO 1133
190°C/5.0 kg	22	g/10 min	ISO 1133
抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型)	90.0	hr	内部方法

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	65		ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量 (2.00 mm, 模压成型)	1450	MPa	ISO 527-2/1BA/50
拉伸应力			ISO 527-2/1BA/50
屈服, 2.00 mm, 模压成型	32.0	MPa	ISO 527-2/1BA/50
断裂, 2.00 mm, 模压成型	15.0	MPa	ISO 527-2/1BA/50
拉伸应变 (断裂, 2.00 mm, 模压成型)	> 200	%	ISO 527-2/1BA/50
弯曲模量 (2.00 mm, 模压成型)	1700	MPa	ISO 178
弯曲应力 (2.00 mm, 模压成型)	32.0	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (23°C, 模压成型)	4.0	kJ/m2	ISO 180/A

热性能	额定值	单位制	测试方法
热变形温度 (0.45 MPa, 未退火)	95.0	°C	ISO 75-2/B
维卡软化温度	129	°C	ISO 306/A
溶融温度（DSC）	135	°C	ISO 11357-3
Enthalpy Change	229	J/g	ISO 11357-3

注射	额定值	单位制
加工（熔体）温度	230 到 275	°C
模具温度	32.0 到 38.0	°C
注塑压力	69.0 到 89.0	MPa

物性表.jpg