DuPont Performance Polymers Zytel? 84G33 BKB031 Nylon 66 (Unverified Data**)
Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 30% Glass Fiber Filled
DuPont Performance Polymers
产品说明:
Zytel? 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was developed for applications requiring strength, stiffness and impact resistance along with good surface appearance.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel? 84G33 BKB031 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.34 g/cc | 0.0484 lb/in3 | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.0010 cm/cm
@Thickness 2.00 mm
|
0.0010 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.0060 cm/cm
@Thickness 2.00 mm
|
0.0060 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 53 | 53 | 50%RH; ISO 2039/2 |
| 81 | 81 | DAM; ISO 2039/2 | |
| 洛氏硬度（R 级） | 113 | 113 | 50%RH; ISO 2039/2 |
| 116 | 116 | DAM; ISO 2039/2 | |
| 抗张强度(断裂) | 60.0 MPa
@Temperature 150 °C
|
8700 psi
@Temperature 302 °F
|
50%RH; ISO 527 |
| 66.0 MPa
@Temperature 120 °C
|
9570 psi
@Temperature 248 °F
|
50%RH; ISO 527 | |
| 67.0 MPa
@Temperature 150 °C
|
9720 psi
@Temperature 302 °F
|
DAM; ISO 527 | |
| 71.0 MPa
@Temperature 100 °C
|
10300 psi
@Temperature 212 °F
|
50%RH; ISO 527 | |
| 75.0 MPa
@Temperature 120 °C
|
10900 psi
@Temperature 248 °F
|
DAM; ISO 527 | |
| 77.0 MPa
@Temperature 80.0 °C
|
11200 psi
@Temperature 176 °F
|
50%RH; ISO 527 | |
| 82.0 MPa
@Temperature 100 °C
|
11900 psi
@Temperature 212 °F
|
DAM; ISO 527 | |
| 84.0 MPa
@Temperature 60.0 °C
|
12200 psi
@Temperature 140 °F
|
50%RH; ISO 527 | |
| 90.0 MPa
@Temperature 80.0 °C
|
13100 psi
@Temperature 176 °F
|
DAM; ISO 527 | |
| 102 MPa
@Temperature 60.0 °C
|
14800 psi
@Temperature 140 °F
|
DAM; ISO 527 | |
| 115 MPa
@Temperature 23.0 °C
|
16700 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 144 MPa
@Temperature 0.000 °C
|
20900 psi
@Temperature 32.0 °F
|
50%RH; ISO 527 | |
| 150 MPa
@Temperature 23.0 °C
|
21800 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 167 MPa
@Temperature 0.000 °C
|
24200 psi
@Temperature 32.0 °F
|
DAM; ISO 527 | |
| 205 MPa
@Temperature -40.0 °C
|
29700 psi
@Temperature -40.0 °F
|
50%RH; ISO 527 | |
| 220 MPa
@Temperature -40.0 °C
|
31900 psi
@Temperature -40.0 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | 4.0 %
@Temperature 23.0 °C
|
4.0 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 5.4 %
@Temperature -40.0 °C
|
5.4 %
@Temperature -40.0 °F
|
50%RH; ISO 527 | |
| 5.5 %
@Temperature 0.000 °C
|
5.5 %
@Temperature 32.0 °F
|
DAM; ISO 527 | |
| 5.7 %
@Temperature 0.000 °C
|
5.7 %
@Temperature 32.0 °F
|
50%RH; ISO 527 | |
| 6.0 %
@Temperature -40.0 °C
|
6.0 %
@Temperature -40.0 °F
|
DAM; ISO 527 | |
| 8.5 %
@Temperature 60.0 °C
|
8.5 %
@Temperature 140 °F
|
DAM; ISO 527 | |
| 8.6 %
@Temperature 23.0 °C
|
8.6 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 9.2 %
@Temperature 60.0 °C
|
9.2 %
@Temperature 140 °F
|
50%RH; ISO 527 | |
| 9.5 %
@Temperature 80.0 °C
|
9.5 %
@Temperature 176 °F
|
50%RH; ISO 527 | |
| 9.5 %
@Temperature 100 °C
|
9.5 %
@Temperature 212 °F
|
50%RH; ISO 527 | |
| 9.6 %
@Temperature 80.0 °C
|
9.6 %
@Temperature 176 °F
|
DAM; ISO 527 | |
| 10 %
@Temperature 100 °C
|
10 %
@Temperature 212 °F
|
DAM; ISO 527 | |
| 10.3 %
@Temperature 120 °C
|
10.3 %
@Temperature 248 °F
|
50%RH; ISO 527 | |
| 10.7 %
@Temperature 120 °C
|
10.7 %
@Temperature 248 °F
|
DAM; ISO 527 | |
| 11.2 %
@Temperature 150 °C
|
11.2 %
@Temperature 302 °F
|
50%RH; ISO 527 | |
| 11.6 %
@Temperature 150 °C
|
11.6 %
@Temperature 302 °F
|
DAM; ISO 527 | |
| 拉伸模量 | 3.746 GPa
@Temperature 150 °C
|
543.3 ksi
@Temperature 302 °F
|
50%RH; ISO 527 |
| 4.052 GPa
@Temperature 150 °C
|
587.7 ksi
@Temperature 302 °F
|
DAM; ISO 527 | |
| 4.223 GPa
@Temperature 120 °C
|
612.5 ksi
@Temperature 248 °F
|
50%RH; ISO 527 | |
| 4.384 GPa
@Temperature 120 °C
|
635.8 ksi
@Temperature 248 °F
|
DAM; ISO 527 | |
| 4.70 GPa
@Temperature 100 °C
|
682 ksi
@Temperature 212 °F
|
50%RH; ISO 527 | |
| 4.956 GPa
@Temperature 100 °C
|
718.8 ksi
@Temperature 212 °F
|
DAM; ISO 527 | |
| 5.182 GPa
@Temperature 80.0 °C
|
751.6 ksi
@Temperature 176 °F
|
50%RH; ISO 527 | |
| 5.518 GPa
@Temperature 60.0 °C
|
800.3 ksi
@Temperature 140 °F
|
50%RH; ISO 527 | |
| 5.614 GPa
@Temperature 80.0 °C
|
814.2 ksi
@Temperature 176 °F
|
DAM; ISO 527 | |
| 6.905 GPa
@Temperature 60.0 °C
|
1001 ksi
@Temperature 140 °F
|
DAM; ISO 527 | |
| 6.929 GPa
@Temperature 23.0 °C
|
1005 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 9.00 GPa
@Temperature 23.0 °C
|
1310 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 9.074 GPa
@Temperature 0.000 °C
|
1316 ksi
@Temperature 32.0 °F
|
DAM; ISO 527 | |
| 9.286 GPa
@Temperature 0.000 °C
|
1347 ksi
@Temperature 32.0 °F
|
50%RH; ISO 527 | |
| 9.426 GPa
@Temperature -40.0 °C
|
1367 ksi
@Temperature -40.0 °F
|
DAM; ISO 527 | |
| 10.234 GPa
@Temperature -40.0 °C
|
1484.3 ksi
@Temperature -40.0 °F
|
50%RH; ISO 527 | |
| 弯曲模量 | 3.167 GPa
@Temperature 150 °C
|
459.3 ksi
@Temperature 302 °F
|
50%RH; ISO 178 |
| 3.33 GPa
@Temperature 150 °C
|
483 ksi
@Temperature 302 °F
|
DAM; ISO 178 | |
| 3.461 GPa
@Temperature 120 °C
|
502.0 ksi
@Temperature 248 °F
|
50%RH; ISO 178 | |
| 3.502 GPa
@Temperature 120 °C
|
507.9 ksi
@Temperature 248 °F
|
DAM; ISO 178 | |
| 3.633 GPa
@Temperature 100 °C
|
526.9 ksi
@Temperature 212 °F
|
50%RH; ISO 178 | |
| 3.651 GPa
@Temperature 100 °C
|
529.5 ksi
@Temperature 212 °F
|
DAM; ISO 178 | |
| 3.737 GPa
@Temperature 80.0 °C
|
542.0 ksi
@Temperature 176 °F
|
50%RH; ISO 178 | |
| 3.982 GPa
@Temperature 80.0 °C
|
577.5 ksi
@Temperature 176 °F
|
DAM; ISO 178 | |
| 4.006 GPa
@Temperature 60.0 °C
|
581.0 ksi
@Temperature 140 °F
|
50%RH; ISO 178 | |
| 4.461 GPa
@Temperature 60.0 °C
|
647.0 ksi
@Temperature 140 °F
|
DAM; ISO 178 | |
| 5.60 GPa
@Temperature 23.0 °C
|
812 ksi
@Temperature 73.4 °F
|
50%RH; ISO 178 | |
| 7.683 GPa
@Temperature 23.0 °C
|
1114 ksi
@Temperature 73.4 °F
|
DAM; ISO 178 | |
| 7.723 GPa
@Temperature -40.0 °C
|
1120 ksi
@Temperature -40.0 °F
|
DAM; ISO 178 | |
| 7.859 GPa
@Temperature 0.000 °C
|
1140 ksi
@Temperature 32.0 °F
|
DAM; ISO 178 | |
| 8.042 GPa
@Temperature -40.0 °C
|
1166 ksi
@Temperature -40.0 °F
|
50%RH; ISO 178 | |
| 8.082 GPa
@Temperature 0.000 °C
|
1172 ksi
@Temperature 32.0 °F
|
50%RH; ISO 178 | |
| 悬壁梁缺口冲击强度 | 12.0 kJ/m2
@Temperature -40.0 °C
|
5.71 ft-lb/in2
@Temperature -40.0 °F
|
50%RH; ISO 180/1A |
| 15.0 kJ/m2
@Temperature -40.0 °C
|
7.14 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 180/1A | |
| 21.0 kJ/m2
@Temperature 23.0 °C
|
9.99 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A |