DuPont Performance Polymers Zytel? 7335F NC010 Nylon 6 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.13 g/cc | 0.0408 lb/in3 | DAM; ISO 1183 |
| Water Absorption | 3.0 %
@Temperature 23.0 °C
|
3.0 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 9.0 %
@Temperature 23.0 °C
|
9.0 %
@Temperature 73.4 °F
|
Saturation, immersed; DAM; ISO 62, Similar to | |
| 线性成型收缩率 | 0.0075 cm/cm
@Thickness 1.60 mm
|
0.0075 in/in
@Thickness 0.0630 in
|
DAM |
| 0.010 cm/cm
@Thickness 3.20 mm
|
0.010 in/in
@Thickness 0.126 in
|
DAM | |
| 线性成型收缩率,Flow | 0.0060 cm/cm
@Thickness 2.00 mm
|
0.0060 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.0080 cm/cm
@Thickness 2.00 mm
|
0.0080 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 55.0 MPa
@Temperature 23.0 °C
|
7980 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 90.0 MPa
@Temperature 23.0 °C
|
13100 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | 9.0 %
@Temperature 23.0 °C
|
9.0 %
@Temperature 73.4 °F
|
DAM; nominal; ISO 527 |
| 15 %
@Temperature 23.0 °C
|
15 %
@Temperature 73.4 °F
|
50mm/min; DAM; ISO 527 | |
| = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
50mm/min; 50%RH; ISO 527 | |
| = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
50%RH; nominal; ISO 527 | |
| Elongation at Yield | 3.8 %
@Temperature 23.0 °C
|
3.8 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 24 %
@Temperature 23.0 °C
|
24 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 拉伸模量 | 1.40 GPa
@Temperature 23.0 °C
|
203 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 3.60 GPa
@Temperature 23.0 °C
|
522 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 简支梁无缺口冲击强度 | 6.00 J/cm2
@Temperature -30.0 °C
|
28.6 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eU |
| 7.00 J/cm2
@Temperature 23.0 °C
|
33.3 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eU | |
| 11.0 J/cm2
@Temperature -30.0 °C
|
52.3 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eU | |
| 12.0 J/cm2
@Temperature 23.0 °C
|
57.1 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.250 J/cm2
@Temperature -30.0 °C
|
1.19 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eA |
| 0.300 J/cm2
@Temperature -30.0 °C
|
1.43 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eA | |
| 0.450 J/cm2
@Temperature 23.0 °C
|
2.14 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA | |
| 1.80 J/cm2
@Temperature 23.0 °C
|
8.57 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+11 ohm-cm
@Temperature 23.0 °C
|
1.00e+11 ohm-cm
@Temperature 73.4 °F
|
50%RH; ASTM D257 |
| 1.00e+11 ohm-cm
@Temperature 23.0 °C
|
1.00e+11 ohm-cm
@Temperature 73.4 °F
|
50%RH; IEC 60093 | |
| = 1.00e+15 ohm-cm
@Temperature 23.0 °C
|
= 1.00e+15 ohm-cm
@Temperature 73.4 °F
|
DAM; IEC 60093 | |
| 1.00e+17 ohm-cm
@Temperature 23.0 °C
|
1.00e+17 ohm-cm
@Temperature 73.4 °F
|
DAM; ASTM D257 | |
| 1.00e+17 ohm-cm
@Temperature 23.0 °C
|
1.00e+17 ohm-cm
@Temperature 73.4 °F
|
DAM; IEC 60093 | |
| Surface Resistance | 1.00e+11 ohm
@Temperature 23.0 °C
|
1.00e+11 ohm
@Temperature 73.4 °F
|
50%RH; ASTM D257 |
| 1.00e+11 ohm
@Temperature 23.0 °C
|
1.00e+11 ohm
@Temperature 73.4 °F
|
50%RH; IEC 60093 | |
| 1.00e+13 ohm
@Temperature 23.0 °C
|
1.00e+13 ohm
@Temperature 73.4 °F
|
DAM; ASTM D257 | |
| 介电常数 | 3.3
@Frequency 1.00e+6 Hz, Temperature 23.0 °C
|
3.3
@Frequency 1.00e+6 Hz, Temperature 73.4 °F
|
DAM; ASTM D150 |
| 3.6
@Frequency 100 Hz, Temperature 23.0 °C
|
3.6
@Frequency 100 Hz, Temperature 73.4 °F
|
DAM; ASTM D150 | |
| 3.6
@Frequency 1000 Hz, Temperature 23.0 °C
|
3.6
@Frequency 1000 Hz, Temperature 73.4 °F
|
DAM; ASTM D150 | |
| 4.2
@Frequency 100 Hz, Temperature 23.0 °C
|
4.2
@Frequency 100 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 | |
| 介电强度 | 13.5 kV/mm
@Thickness 3.20 mm, Temperature 23.0 °C
|
343 kV/in
@Thickness 0.126 in, Temperature 73.4 °F
|
50%RH; Short Time; ASTM D149 |
| 16.3 kV/mm
@Thickness 3.20 mm, Temperature 23.0 °C
|
414 kV/in
@Thickness 0.126 in, Temperature 73.4 °F
|
DAM; Short Time; ASTM D149 | |
| 耗散因数 | 0.010
@Frequency 1000 Hz, Temperature 23.0 °C
|
0.010
@Frequency 1000 Hz, Temperature 73.4 °F
|
DAM; ASTM D150 |
| 0.010
@Frequency 100 Hz, Temperature 23.0 °C
|
0.010
@Frequency 100 Hz, Temperature 73.4 °F
|
DAM; ASTM D150 | |
| 0.020
@Frequency 1.00e+6 Hz, Temperature 23.0 °C
|
0.020
@Frequency 1.00e+6 Hz, Temperature 73.4 °F
|
DAM; ASTM D150 | |
| 0.030
@Frequency 100 Hz, Temperature 23.0 °C
|
0.030
@Frequency 100 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 | |
| 0.11
@Frequency 1.00e+6 Hz, Temperature 23.0 °C
|
0.11
@Frequency 1.00e+6 Hz, Temperature 73.4 °F
|
50%RH; ASTM D150 | |
| 0.23
@Frequency 1000 Hz, Temperature 23.0 °C
|
0.23
@Frequency 1000 Hz, Temperature 73.4 °F
|
50%RH; ASTM D150 | |
| 0.37
@Frequency 100 Hz, Temperature 23.0 °C
|
0.37
@Frequency 100 Hz, Temperature 73.4 °F
|
50%RH; ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | 600 V
@Temperature 23.0 °C
|
600 V
@Temperature 73.4 °F
|
DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 |
| 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 线性热膨胀系数,横向流动 | 92.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
51.1 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 |
| 92.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
51.1 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 熔融温度 | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 175 °C | 347 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 |
| 可燃性(UL94) | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; UL94 |
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; IEC 60695-11-10 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 260 - 280 °C | 500 - 536 °F | DAM |
| 270 °C | 518 °F | DAM; Optimum | |
| 模具温度 | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | = 0.20 % | = 0.20 % | DAM |