苏州劳伦维斯塑化有限公司
............................................................................................................................... ......................................................................................................................................... .............................................................. 
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 饱和(23℃) | ASTM D-570 | ||
| DAM｜50%RH | |||||
| 8.5｜- | |||||
| % | |||
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | |
| DAM｜50%RH | DAM｜50%RH | ||
| %1.2｜- | 1.2｜- |
| % | ||||
| 物理性能 | 比重 | ASTM D-792 | ||
| DAM｜50%RH | ||||
| 1.14｜1.14 |
| 泰伯磨耗量 | cs-17 Wheel,1000g | ||
| DAM｜50%RH | |||
| -｜7 |
| mg/1000 cycles | ||||
| 机械性能 | 断裂伸长率 | 23℃ | ASTM D-638 | |
| DAM｜50%RH | ||||
| 60｜≥300 |
| % | |||
| 硬度计硬度 | ASTM D-676 | ||
| DAM｜50%RH | |||
| 89｜82 |
| 洛氏硬度R | ASTM D-785 | ||
| DAM｜50%RH | |||
| R121｜R108 |
| 洛氏硬度M | ASTM D-785 | ||
| DAM｜50%RH | |||
| M79｜M59 |
| 剪切强度 | 23℃ | ASTM D-732 | |
| DAM｜50%RH | |||
| 66.2｜- |
| MPa | |||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | |
| DAM｜50%RH | |||
| 53｜112 |
| j/m | |||
| 揉曲模量 | 23℃ | ASTM D-790 | |
| DAM｜50%RH | |||
| 2827｜1207 |
| MPa | |||
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | |
| DAM｜50%RH | |||
| 504｜1470 |
| 1%形变时的压应力 | ASTM D-695 | ||
| DAM｜50%RH | |||
| 33.8｜- |
| MPa | |||
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | |
| DAM｜50%RH | |||
| 157｜231 |
| KJ/m2 | |||
| 屈服伸长率 | ASTM D-638 | ||
| DAM｜50%RH | |||
| 5｜25 |
| % | |||
| 拉伸强度 | 23℃ | ASTM D-638 | |
| DAM｜50%RH | |||
| 82.7｜77.2 |
| MPa | |||
| 熔点结晶 | ASTM D-2177 | ||
| DAM｜50%RH | |||
| 270｜- |
| ℃ | |||
| 屈服强度 | 23℃ | ||
| DAM｜50%RH | |||
| 82.7｜58.6 |
| MPa | ||||
| 电气性能 | 介电常数 | 100Hz(cps) | ASTM D-178 | |
| DAM｜50%RH | ||||
| 4.0｜8.0 |
| 耗散因数 | 103Hz(cps) | ASTM D-150 | |
| DAM｜50%RH | |||
| 0.02｜0.2 |
| 介电常数 | 103Hz(cps) | ASTM D-150 | |
| DAM｜50%RH | |||
| 3.9｜7.0 |
| 介电常数 | 106Hz(cps) | ASTM D-150 | |
| DAM｜50%RH | |||
| 3.6｜4.6 |
| 体积电阻率 | ASTM D-257 | ||
| DAM｜50%RH | |||
| 1015｜1013 |
| Ω.cm | |||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | |
| DAM｜50%RH | |||
| 0.01｜0.2 |
| 耗散因数 | 106Hz(cps) | ASTM D-150 | |
| DAM｜50%RH | |||
| 0.02｜0.1 |
| 热性能 | 线性热膨胀系数 | ASTM D-696 | ||
| DAM｜50%RH | ||||
| 7×10-5｜- |
| m/m/℃ | |||
| UL可燃性导级 | UL 94 | ||
| DAM｜50%RH | |||
| 94｜V-2 |
| 熔点 | Fisher Johns法 | ASTM D-789 | |
| DAM｜50%RH | |||
| 255｜255 |
| ℃ | |||
| 热畸变温度 | 18×106Pa | ASTM D-648 | |
| DAM｜50%RH | |||
| 90｜- |
| ℃ | |||
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | |
| DAM｜50%RH | |||
| 235｜- |
| ℃ | |||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | |
| DAM｜50%RH | |||
| 1.4｜- |
| % | |||
| 导热系数 | |||
| DAM｜50%RH | |||
| 0.25｜- |
| w/mk | |||
| 脆化温度 | ASTM D-746 | ||
| DAM｜50%RH | |||
| -80｜-65 |
| ℃ | ||||
| 其它性能 | 需氧指数 | ASTM D-2863 | ||
| DAM｜50%RH | ||||
| 28｜31 |
| % |