苏州寅旭塑化有限公司
Zytel FG70G50HSR2 BK309
NYLON RESIN
PA66-GF30
CHARACTERISTICS
Regional availability
- Global
Processing
Injection Molding
Delivery form
Pellets
Additives
Release agent
Special characteristics
Heat stabilized or stable to heat, Hydrolysis resistant
PRODUCT TEXT
Zytel? FG70G30HSR2 BK309 is a 30% Glass Reinforced, Heat Stabilized, Polyamide 66
PRODUCT INFORMATION
DRY/COND.
TEST NORM
Resin Identification,
PA66-GF30
ISO 1043
Part Marking Code,
>PA66-GF30<
ISO 11469
ISO designation,
ISO 16396-PA66,GF30,M1CGHRW,S14-100
-
REGULATORY
Substance of Very High Concern Report
RHEOLOGICAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Viscosity number,
158/*
cm3/g
ISO 307, 1157, 1628
Molding shrinkage, parallel
0.2/-
%
ISO 294-4, 2577
Molding shrinkage, normal
1.0/-
%
ISO 294-4, 2577
MECHANICAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Tensile Modulus,
10000/7000
MPa
ISO 527-1/-2
Stress at break,
200/130
MPa
ISO 527-1/-2
Strain at break,
3.3/5
%
ISO 527-1/-2
Charpy impact strength, 73°F
70/80
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 73°F
12/15
kJ/m2
ISO 179/1eA
Poisson"s ratio,
0.34/0.35
-
-
THERMAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Melting temperature, 18°F/min
263/*
°C
ISO 11357-1/-3
Glass transition temperature, 18°F/min
75/20
°C
ISO 11357-1/-2
Temp. of deflection under load, 260 psi
250/*
°C
ISO 75-1/-2
Temp. of deflection under load, 65 psi
260/*
°C
ISO 75-1/-2
Vicat softening temperature, 90°F/h, 11 lbf
209/*
°C
ISO 306
Coeff. of linear therm. expansion, parallel
28/*
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, normal
95/*
E-6/K
ISO 11359-1/-2
Thermal conductivity of melt,
0.22
W/(m K)
-
Eff. thermal diffusivity,
6.85E-8
m2/s
-
Spec. heat capacity of melt,
2220
J/(kg K)
-
FLAMMABILITY
DRY/COND.
UNIT
TEST NORM
Oxygen index,
24/*
%
ISO 4589-1/-2
FMVSS Class,
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
<80
mm/min
ISO 3795 (FMVSS 302)
ELECTRICAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Surface resistivity,
*/1E13
Ohm
IEC 62631-3-2
OTHER PROPERTIES
DRY/COND.
UNIT
TEST NORM
Density,
1370/-
kg/m3
ISO 1183
Density of melt,
1200
kg/m3
-
INJECTION
DRY/COND.
UNIT
Drying Recommended,
yes
Drying Temperature,
80
°C
Drying Time, Dehumidified Dryer,
2 - 4
h
Processing Moisture Content,
≤0.2
%
Melt Temperature Optimum,
295
°C
Min. melt temperature,
285
°C
Max. melt temperature,
305
°C
Max. screw tangential speed,
0.2
m/s
Mold Temperature Optimum,
100
°C
Min. mold temperature,
50
°C
Max. mold temperature,
120
°C
Hold pressure range,
50 - 100
MPa
Hold pressure time,
3
s/mm
Ejection temperature,
210
°C
CHEMICAL MEDIA RESISTANCE
Acids
Acetic Acid (5% by mass), 23°C
Citric Acid solution (10% by mass), 23°C
Lactic Acid (10% by mass), 23°C
Hydrochloric Acid (36% by mass), 23°C
Nitric Acid (40% by mass), 23°C
Sulfuric Acid (38% by mass), 23°C
Sulfuric Acid (5% by mass), 23°C
Chromic Acid solution (40% by mass), 23°C
Bases
Sodium Hydroxide solution (35% by mass), 23°C
Sodium Hydroxide solution (1% by mass), 23°C
Ammonium Hydroxide solution (10% by mass), 23°C
Alcohols
Isopropyl alcohol, 23°C
Methanol, 23°C
Ethanol, 23°C
Hydrocarbons
n-Hexane, 23°C
Toluene, 23°C
iso-Octane, 23°C
Ketones
Acetone, 23°C
Ethers
Diethyl ether, 23°C
Mineral oils
Insulating Oil, 23°C
Salt solutions
Sodium Chloride solution (10% by mass), 23°C
Sodium Hypochlorite solution (10% by mass), 23°C
Sodium Carbonate solution (20% by mass), 23°C
Sodium Carbonate solution (2% by mass), 23°C
Zinc Chloride solution (50% by mass), 23°C
Other
Ethyl Acetate, 23°C
Hydrogen peroxide, 23°C
Ethylene Glycol (50% by mass) in water, 108°C
1% nonylphenoxy-polyethyleneoxy ethanol in water, 23°C
50% Oleic acid 50% Olive Oil, 23°C
Water, 23°C
Water, 90°C
Phenol solution (5% by mass), 23°C