东莞市塑宇化工有限公司
100AF
POM | 聚甲醛#赛钢
美国杜邦
100AF 物性表
| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 密度 | 1.54 | ASTM D-792 |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 扩散因数 (+73℉(+23℃)106Hz) | 0.009 | ASTM D-150 | |
| 绝缘系数 (+73℉(+23℃)102to106Hz) | 3.1 | ASTM D-150 | |
| 电阻系数 (+73℉(+23℃)0.2%H2O) | 3×10 | ohm-cm | ASTM D-257 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 伸张强度 (+23℃) | 52.4 | MPa | ASTM D-638 |
| 压缩应力 (+23℃@1%Def.) | 31.0 | MPa | ASTM D-695 |
| 拉力冲击抵抗力 (+73℉) | 50 | ft.lb/in | D1822Long |
| 绝缘强度 (Short Time,90 mils) | 400(125mils) | V/mil | ASTM D-149 |
| 压缩应力 | ASTM D-695 | ||
| (+73°F@1%Def.) | 4.5 | MPsi | |
| (+73°F@10%Def.) | 13.0 | MPsi | |
| 弯曲疲劳忍耐限度 (+23℃) | 24.8 | MPa | ASTM D-671 |
| 挠曲系数 | 在25℃下 | ||
| (+158℉) | 190 | MPsi | |
| (+73℉) | 340 | MPsi | |
| 伸张强度 (+212℉) | 4.0 | MPsi | ASTM D-638 |
| 弯曲降服强 (+23℃) | 72.4 | MPa | ASTM D-790 |
| IZOD冲击强度 (40℃) | 53.4 | j/m | ASTM D-256 |
| 弹性系数 (+73℉) | 420 | MPsi | ASTM D-638 |
| 断裂时之拉力伸张度 (+212℉(+100℃)) | 250 | % | ASTM D-638 |
| 伸张强度 (+100℃) | 28.3 | MPa | ASTM D-638 |
| 断裂时之拉力伸张度 (+73℉(+23℃)) | 22 | % | ASTM D-638 |
| 拉力冲击抵抗力 (+23℃) | 102 | kj/m | D1822Long |
| 热变形温度 (66psi) | 334 | ℉ | ASTM D-648 |
| 挠曲系数 | 在25℃下 | ||
| (+250℉) | 80 | MPsi | |
| (+70℃) | 1310 | MPa | |
| 电弧抵抗力 (120mil(3.1mm)) | 183no tracking | Sec. | ASTM D-495 |
| 洛氏硬度 | M78,R118 | ASTM D-785 | |
| 剪力 (+73℉) | 8.0 | MPsi | ASTM D-732 |
| 弯曲疲劳忍耐限度 (+73℉) | 3.6 | MPsi | ASTM D-671 |
| 剪力 (+23℃) | 55.2 | MPa | ASTM D-732 |
| 挠曲系数 (-68℉) | 520 | MPsi | 在25℃下 |
| 绝缘强度 (Short Time,2.3mm) | 15.8(3.2mm) | MV/m | ASTM D-149 |
| 伸张强度 (+250℉) | 3.1 | MPsi | ASTM D-638 |
| 断裂时之拉力伸张度 (-68℉(-55℃)) | 15 | % | ASTM D-638 |
| 伸张强度 (+158℉) | 5.3 | MPsi | ASTM D-638 |
| 负载下之变形 (2000psi@+122℉(14Mpa@50℃)) | 0.6 | % | ASTM D-621 |
| 挠曲系数 | 在25℃下 | ||
| (+23℃) | 2340 | MPa | |
| (+122℃) | 550 | MPa | |
| 弯曲降服强 (+73℉) | 10.5 | MPsi | ASTM D-790 |
| 伸张强度 (+122℃) | 20.7 | MPa | ASTM D-638 |
| IZOD冲击强度 (+73℉) | 1.2 | ft.lb/in | ASTM D-256 |
| 摩擦系数 (+73℉(+23℃)动态) | 0.14 | ThrustWasherTest | |
| 挠曲系数 (+212℉) | 110 | MPsi | 在25℃下 |
| 断裂时之拉力伸张度 (+158℉(+70℃)) | 50 | % | ASTM D-638 |
| 挠曲系数 (+100℃) | 700 | MPa | 在25℃下 |
| 伸张强度 (+73℉) | 7.6 | MPsi | ASTM D-638 |
| IZOD冲击强度 (-40℉) | 1.0 | ft.lb/in | ASTM D-256 |
| 伸张强度 | ASTM D-638 | ||
| (+70℃) | 36.5 | MPa | |
| (-68℉) | 10.9 | MPsi | |
| 弹性系数 (+23℃) | 2895 | MPa | ASTM D-638 |
| 挠曲系数 (-55℃) | 3585 | MPa | 在25℃下 |
| 压缩应力 (+23℃@10%Def.) | 89.6 | MPa | ASTM D-695 |
| 断裂时之拉力伸张度 (+250℉(+122℃)) | >260 | % | ASTM D-638 |
| IZOD冲击强度 (+23℃) | 64.1 | j/m | ASTM D-256 |
| 伸张强度 (-55℃) | 75 | MPa | ASTM D-638 |
| 加工性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 吸水量 | ASTM D-570 | ||
| (浸泡均衡点+73℉(+23℃)) | 0.72 | % | |
| (Equil.50%R.h.+73℉(+23℃)) | 0.18 | % | |
| (24hrs浸泡+73℉(+23℃)) | 0.20 | % |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热变形温度 | ASTM D-648 | ||
| (0.5MPa) | 168 | ℃ | |
| (1.8MPa) | 118 | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | ||
| (-40 to +29℃) | 10.4 | 10-5m/m.℃ | |
| (-40 to +85℉) | 5.8 | 10-5in/in℉ | |
| (+29 to +60℃) | 12.2 | 10-5m/m.℃ | |
| 熔点 | 347 | ℉ | ASTM D-2133 |
| 可燃烧性 | 94HB | UL-94 | |
| 热变形温度 (264psi) | 244 | °F | ASTM D-648 |
| 线性热膨胀系数 (+85 to +140℉) | 6.8 | 10-5in/in℉ | ASTM D-696 |
| 熔点 | 175 | ℃ | ASTM D-2133 |