苏州寅旭塑化有限公司
Zytel? 79G13HSL BK039
NYLON RESIN
PA66-I-GF13
Special characteristics
Heat stabilized or stable to heat
PRODUCT TEXT
Common features of Zytel? nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel? nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel? nylon resin, including most flame retardant grades, offer the ability to be coloured.
The good melt stability of Zytel? nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Zytel? nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
Zytel? 79G13HSL BK039 is a 13 % glass reinforced, heat stabilized, lubricated slightly toughened black polyamide 66 for injection molding. It has improved impact resistance.
PRODUCT INFORMATION
DRY/COND.
TEST NORM
Resin Identification
PA66-IGF13
ISO 1043
Part Marking Code
>PA66-IGF13<
ISO 11469
ISO designation
ISO 16396-PA66-I,GF13,M1CGHR,S18-050
-
REGULATORY
Substance of Very High Concern Report
RHEOLOGICAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Viscosity number
163/*
cm3/g
ISO 307, 1157, 1628
Molding shrinkage, parallel
0.5/-
%
ISO 294-4, 2577
Molding shrinkage, normal
0.8/-
%
ISO 294-4, 2577
MECHANICAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Tensile Modulus
5100/3700
MPa
ISO 527-1/-2
Stress at break
115/67
MPa
ISO 527-1/-2
Strain at break
4/10
%
ISO 527-1/-2
Charpy impact strength, 73°F
67/59
kJ/m2
ISO 179/1eU
Charpy impact strength, -22°F
59/54
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 73°F
8/12
kJ/m2
ISO 179/1eA
Charpy notched impact strength, -22°F
6/6
kJ/m2
ISO 179/1eA
Izod notched impact strength, 73°F
7.5/10
kJ/m2
ISO 180/1A
Poisson's ratio
0.35/0.36
-
-
THERMAL PROPERTIES
DRY/COND.
UNIT
TEST NORM
Melting temperature, 18°F/min
262/*
°C
ISO 11357-1/-3
Temp. of deflection under load, 260 psi
240/*
°C
ISO 75-1/-2
Temp. of deflection under load, 65 psi
260/*
°C
ISO 75-1/-2
RTI, electrical, 30mil
105
°C
UL 746B
RTI, electrical, 60mil
120
°C
UL 746B
RTI, electrical, 120mil
120
°C
UL 746B
RTI, impact, 30mil
65
°C
UL 746B
RTI, impact, 60mil
105
°C
UL 746B
RTI, impact, 120mil
105
°C
UL 746B
RTI, strength, 30mil
105
°C
UL 746B
RTI, strength, 60mil
120/*
°C
UL 746B
RTI, strength, 120mil
120
°C
UL 746B
FLAMMABILITY
DRY/COND.
UNIT
TEST NORM
Burning Behav. at 60mil nom. thickn.
HB/*
class
IEC 60695-11-10
Thickness tested
1.5/*
mm
IEC 60695-11-10
UL recognition
yes/*
-
UL 94
Burning Behav. at thickness h
HB/*
class
IEC 60695-11-10
Thickness tested
0.8/*
mm
IEC 60695-11-10
UL recognition
yes/*
-
UL 94
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
24
mm/min
ISO 3795 (FMVSS 302)
OTHER PROPERTIES
DRY/COND.
UNIT
TEST NORM
Density
1210/-
kg/m3
ISO 1183
VDA PROPERTIES
DRY/COND.
UNIT
TEST NORM
Emission of organic compounds
13
μgC/g
VDA 277
Odor test
4
class
VDA 270
Fogging, G-value (condensate)
0.3/*
mg
ISO 6452
INJECTION
DRY/COND.
UNIT
Drying Recommended
yes
Drying Temperature
80
°C
Drying Time, Dehumidified Dryer
2 - 4
h
Processing Moisture Content
≤0.2
%
Melt Temperature Optimum
295
°C
Min. melt temperature
285
°C
Max. melt temperature
305
°C
Max. screw tangential speed
0.2
m/s
Mold Temperature Optimum
80
°C
Min. mold temperature
50
°C
Max. mold temperature
100
°C
Hold pressure range
50 - 100
MPa
Hold pressure time
3
s/mm
Ejection temperature
210
°C