东莞市铭汇塑胶有限公司
HIPLEX? TR 144
高密度聚乙烯
HIP-PetroHemija
产品说明：
HIPLEX? TR 144, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties.
Application:
HIPLEX? TR-144 is suitable for production of composite films, carrier bags and other kinds of packaging. It is also recommended for blow moulding of small and medium size containers.
HIPLEX? TR-144 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX? TR-144 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia.
Application:
HIPLEX? TR-144 is suitable for production of composite films, carrier bags and other kinds of packaging. It is also recommended for blow moulding of small and medium size containers.
HIPLEX? TR-144 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX? TR-144 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia.
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.947 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.18 | g/10 min | ISO 1133 |
| 抗环境应力开裂 (条件 B, F50) | > 1000 | hr | ISO 22088 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 64 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 | ISO 527-2 | ||
| 屈服 | 21.0 | MPa | ISO 527-2 |
| 断裂 | 32.0 | MPa | ISO 527-2 |
| 拉伸应变 (断裂) | 900 | % | ISO 527-2 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 25 | μm | |
| 拉伸应力 | ISO 527-3 | ||
| MD : 屈服, 25 μm | 24.0 | MPa | ISO 527-3 |
| TD : 屈服, 25 μm | 19.0 | MPa | ISO 527-3 |
| MD : 断裂, 25 μm | 40.0 | MPa | ISO 527-3 |
| TD : 断裂, 25 μm | 32.0 | MPa | ISO 527-3 |
| 伸长率 | ISO 527-3 | ||
| MD : 断裂, 25 μm | 550 | % | ISO 527-3 |
| TD : 断裂, 25 μm | 690 | % | ISO 527-3 |
| 落锤冲击 (25 μm) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.0 μm | 27.0 | kN/m | ASTM D1922 |
| TD : 25.0 μm | 270.3 | kN/m | ASTM D1922 |
| 补充信息 | 额定值 | 单位制 | |
|---|---|---|---|
| 吹气模制温度 2 | 195 到 220 | °C |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 无断裂 | ISO 180 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 124 | °C | ISO 306 |
| 备注 | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blow-up ratio: 3.5-5 : 1, Neck height: 6-10 times die diameter |