PC+PBT MAKROBLEND UT6007

PC+PBT)-blend, impact modified, easy release, UV-stabilized, injection molding grade. Makroblend? UT6007 offers an exceptional low-temperature impact strength, good flowability and excellent chemical resistance.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in3	ISO 1183-1
Moisture Absorption at Equilibrium	0.20 %	0.20 %	ISO 62
Water Absorption at Saturation	0.50 %	0.50 %	ISO 62
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	Post-shrinkage, 1 hr; 90°C; b.o. ISO 2577
	0.0070 - 0.0090 cm/cm	0.0070 - 0.0090 in/in	600 bar; b.o. ISO 2577
Melt Flow	18 g/10 min @Load 5.00 kg, Temperature 260 °C	18 g/10 min @Load 11.0 lb, Temperature 500 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	108 MPa	15700 psi	ISO 2039-1
Tensile Strength at Break	50.0 MPa	7250 psi	50 mm/min; ISO 527-1,-2
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ISO 527-1,-2

PC+PBT MAKROBLEND UT6007

简介：

PC-PBT   是PC与PBT的共混材料，通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象

PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；PBT的优点是它的刚性不受温度的影响，变形小；这样共混后的材料PC-PBT即保留了两者的优点

PC-PBT具有较高的表面硬度，较高的刚性和韧性，也有较高的抗高温形的能力，也有较高的抗应力开裂能力；它的机械性能介于两者之间

抗高温变形对于大型的外壳类材料具有重要的意义。

产品特性：

·高韧性（即使在低温环境中）

·良好的耐化学品性能

·不易发生应力开裂

·良好的涂覆性能

·低吸湿率

用途：

·汽车工程

·电气工程/电子

·照明技术

·运动和休闲

PC+PBT MAKROBLEND UT6007 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！