LG ABS XR401F
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 81.4 MPa @Thickness 3.20 mm |
11800 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.65 GPa @Thickness 3.20 mm |
384 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG ABS XR401F
特性：
ABS同PS一样是一种加工性能优良的热塑性塑料，可用通用的加工方法加工。 ABS的熔体流动性比PVC和PC好，但比PE、PA及PS差，与POM和HIPS类似；ABS的流动特性属非牛顿流体，其熔体粘度对加工温度和剪切速率都有关系，但对剪切速率更为敏感。
ABS的热稳定性好，不易出现降解现象。ABS的吸水性较高，加工前应进行干燥处理。一般制品的干燥条件为温度80~85℃，时间2~4h；对特殊要求的制品（如电镀）的干燥条件为温度70~80℃，时间18~18h。 ABS制品在加工中易产生内应力，内应力的大小可通过浸入冰乙酸中检验；如应力太大和制品对应力开裂绝对禁止，应进行退火处理，具体条件为放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。
用途 ：
ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。 ABS树脂广泛应用于汽车工业.电器仪表工业和机械工业中,常作齿轮,汽车配件,挡泥板,扶手,冰箱内衬,叶片,轴承,把手,管道,接头,仪表壳,仪表板,盆安全帽等:在家用电器和家用电子设备的应用前景更广阔,如电视机,收录机,冰箱,冷柜,洗衣机,空调机,吸尘器和各种小家电器材:日用品有鞋,包,各种旅游箱,办公设备,玩具及各种容器等,低发泡的ABS能代替木材,适合作建材,家具和家庭用品