SABIC Innovative Plastics NORYL N190X PPE+PS
Polymer,Thermoplastic,Polyphenylene Ether/PPO,Polystyrene (PS)
SABIC Innovative Plastics (GE Plastics)
产品说明:
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. RTI Elec/Imp/Str 95/80/95. Dielectric strength. Suitable for E/E market applications.
SABIC Innovative Plastics NORYL N190X PPE+PS 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| 吸水率 | 0.080 %
@Time 86400 sec
|
0.080 %
@Time 24.0 hour
|
ASTM D570 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 | 20 g/10 min
@Load 5.00 kg, Temperature 280 °C
|
20 g/10 min
@Load 11.0 lb, Temperature 536 °F
|
ASTM D1238 |
| 化合物熔体指数 | 23 g/10 min
@Load 5.00 kg, Temperature 280 °C
|
23 g/10 min
@Load 11.0 lb, Temperature 536 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 120 | 120 | ASTM D785 |
| 抗张强度(断裂) | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 9.0 % | 9.0 % | Type I, 50 mm/min; ASTM D638 |
| 9.2 % | 9.2 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 3.2 % | 3.2 % | 50 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.58 GPa | 374 ksi | 50 mm/min; ASTM D638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 87.0 MPa | 12600 psi | 2 mm/min; ISO 178 |
| 91.0 MPa | 13200 psi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.30 GPa | 334 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 2.35 GPa | 341 ksi | 2 mm/min; ISO 178 | |
| 2.50 GPa | 363 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 2.93 J/cm | 5.49 ft-lb/in | ASTM D256 |
| 1.00 J/cm
@Temperature -30.0 °C
|
1.87 ft-lb/in
@Temperature -22.0 °F
|
ASTM D256 | |
| 悬壁梁无缺口冲击强度 | 7.20 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 20.0 kJ/m2 | 9.52 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 简支梁缺口冲击强度 | 2.00 J/cm2 | 9.52 ft-lb/in2 | ISO 179/2C |
| 落锤总能量 | 50.0 J
@Temperature 23.0 °C
|
36.9 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| 泰伯磨损，毫克/1000次 | 76 | 76 | CS-17, 1 kg; ASTM D1044 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.80e+16 ohm-cm | 1.80e+16 ohm-cm | ASTM D257 |
| 介电常数 | 2.6
@Frequency 100000 Hz
|
2.6
@Frequency 100000 Hz
|
ASTM D150 |
| 2.74
@Frequency 100 Hz
|
2.74
@Frequency 100 Hz
|
ASTM D150 | |
| 介电强度 | 19.2 kV/mm
@Thickness 3.20 mm
|
488 kV/in
@Thickness 0.126 in
|
in oil; ASTM D149 |
| 耗散因数 | 0.0055
@Frequency 100000 Hz
|
0.0055
@Frequency 100000 Hz
|
ASTM D150 |
| 0.013
@Frequency 100 Hz
|
0.013
@Frequency 100 Hz
|
ASTM D150 | |
| 耐电弧性 | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 77.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
42.8 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 线性热膨胀系数,横向流动 | 81.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
45.0 μin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 导热系数 | 0.240 W/m-K | 1.67 BTU-in/hr-ft2-°F | ASTM C177 |
| 载荷下热变形温度(0.46 MPa) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 95.0 °C
@Thickness 3.20 mm
|
203 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 78.0 °C
@Thickness 3.20 mm
|
172 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| 86.0 °C
@Thickness 6.40 mm
|
187 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 维卡软化温度 | 104 °C | 219 °F | Rate B/50; ASTM D1525 |
| 107 °C | 225 °F | Rate B/120; ISO 306 | |
| UL RTI | 95.0 °C | 203 °F | UL 746B |
| UL RTI，机械冲击 | 80.0 °C | 176 °F | UL 746B |
| UL RTI，机械无冲击 | 95.0 °C | 203 °F | UL 746B |
| 可燃性(UL94) | HB
@Thickness 1.01 mm
|
HB
@Thickness 0.0398 in
|
UL 94 |
| V-0
@Thickness 1.47 mm
|
V-0
@Thickness 0.0579 in
|
UL 94 | |
| 5VA
@Thickness 2.99 mm
|
5VA
@Thickness 0.118 in
|
UL 94 | |
| 极限氧指数 | 39 % | 39 % | ASTM D2863 |
| 材料描述 | 测试方法 | |
|---|---|---|
| UV-light, water exposure/immersion | F1 | UL 746C |