SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific)
Polymer,Thermoplastic,Polyphenylene Ether/PPO,Polystyrene (PS)
SABIC Innovative Plastics (GE Plastics)
产品说明:
Noryl* N1250 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm and V0-5VA at 2.5 mm with a specific density of 1.11 g/cm^3. Noryl N1250 has a heat Vicat resistance of 137 deg C and it may be an excellent material candidate for application requiring electrically insuNoryl* N1250 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm and V
SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| 密度 | 1.10 g/cc | 0.0397 lb/in3 | ISO 1183 |
| 吸水率 | 0.070 %
@Time 86400 sec
|
0.070 %
@Time 24.0 hour
|
ASTM D570 |
| 水分吸收 | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.25 % | 0.25 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 cm/cm
@Time 86400 sec
|
0.0050 in/in
@Time 24.0 hour
|
ISO 294 |
| 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method | |
| 化合物熔体指数 | 12 g/10 min
@Load 5.00 kg, Temperature 280 °C
|
12 g/10 min
@Load 11.0 lb, Temperature 536 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 68.0 MPa | 9860 psi | SABIC - Japan Method |
| 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 | |
| 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 8.0 % | 8.0 % | 50 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 50 mm/min; ASTM D638 | |
| 45 % | 45 % | SABIC - Japan Method | |
| 屈服伸长率 | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.62 GPa | 380 ksi | 1 mm/min; ISO 527 |
| 2.72 GPa | 395 ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | 107 MPa | 15500 psi | ASTM D790 |
| 109 MPa | 15800 psi | 2 mm/min; ISO 178 | |
| 122 MPa | 17700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.53 GPa | 367 ksi | 2 mm/min; ISO 178 |
| 2.54 GPa | 368 ksi | ASTM D790 | |
| 3.00 GPa | 435 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| 8.00 kJ/m2 | 3.81 ft-lb/in2 | 80*10*4; ISO 180/1A | |
| 6.00 kJ/m2
@Temperature -30.0 °C
|
2.86 ft-lb/in2
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 0.700 J/cm2 | 3.33 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电强度 | 49.0 kV/mm
@Thickness 3.20 mm
|
1240 kV/in
@Thickness 0.126 in
|
in oil; IEC 60243-1 |
| 相比耐漏电起痕指数(CTI) | 250 V | 250 V | IEC 60112 |
| 热丝引燃 (HWI) | >= 120 sec | >= 120 sec | UL 746A |
| 高电弧燃烧，HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | 70.0 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
38.9 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
TMA |
| 线形热膨胀系数 - 流动 | 61.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
33.9 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 |
| 线性热膨胀系数,横向流动 | 68.0 μm/m-°C
@Temperature -40.0 - 40.0 °C
|
37.8 μin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 |
| 载荷下热变形温度(0.46 MPa) | 136 °C
@Thickness 6.40 mm
|
277 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C
@Thickness 6.40 mm
|
257 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 维卡软化温度 | 139 °C | 282 °F | Rate B/120; ISO 306 |
| UL RTI | 110 °C | 230 °F | UL 746B |
| UL RTI，机械冲击 | 105 °C | 221 °F | UL 746B |
| UL RTI，机械无冲击 | 110 °C | 230 °F | UL 746B |
| 可燃性(UL94) | V-2
@Thickness 0.400 mm
|
V-2
@Thickness 0.0157 in
|
UL 94 by SABIC-IP |
| V-0
@Thickness 0.750 mm
|
V-0
@Thickness 0.0295 in
|
UL 94 | |
| 5VB
@Thickness 2.50 mm
|
5VB
@Thickness 0.0984 in
|
UL 94 by SABIC-IP | |
| 5VA
@Thickness 2.50 mm
|
5VA
@Thickness 0.0984 in
|
UL 94 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Ball Pressure Test, 125?°C +/- 2?°C | Pass |
IEC 60695-10-2 |