余姚得亿塑化有限公司
原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D792 | 1.20 | ||
| 熔流率 | 300℃/1.2kg | ASTM D1238 | 10 | g/10min | |
| 成型收缩率 | ASTM D955 | 0.005-0.007 | in/in | ||
| 吸水率 | 73℉,24hr | ASTM D570 | 0.15 | % | |
| 73℉,50%RH | ASTM D570 | 0.32 | % | ||
| 机械性能 | 拉伸模量 | ASTM D638 | 350000 | psi | |
| 抗张强度 | 屈服 | ASTM D638 | 8700 | psi | |
| 断裂 | ASTM D638 | 10300 | psi | ||
| 拉伸伸长 | 屈服 | ASTM D638 | 6.0 | % | |
| 断裂 | ASTM D638 | 150 | % | ||
| 弯曲模量 | ASTM D790 | 350000 | psi | ||
| 弯曲强度 | ASTM D790 | 13900 | psi | ||
| 耐磨耗性 | ASTM D1004 | 45 | % | ||
| 悬臂梁缺口冲击 | 73℉,0.126in | ASTM D2566 | 17 | ft.lb/in | |
| 悬臂梁无缺口冲击 | 73℉ | ASTM D256 | 无断裂 | ||
| 仪表化落锤冲击 | 73℉,0.126in | ASTM D3763 | 770 | in/lb | |
| 洛氏硬度 | M-Scale | ASTM D785 | 73 | ||
| R-Scale | ASTM D785 | 118 | |||
| 热性能 | 热变形温度 | 66psi,0.157in,退火 | ASTM D648 | 291 | ℉ |
| 264psi,0.157in,未退火 | ASTM D648 | 262 | ℉ | ||
| 264psi,0.157in,退火 | ASTM D648 | 286 | ℉ | ||
| 维卡软化温度 | ASTM D1525 | 300 | ℉ | ||
| 球压温度 | ASTM D60598-1 | ＞257 | ℉ | ||
| 线性膨胀系数 | -40到180℉ | ASTM D696 | 0.000038 | in/in/℉ | |
| 电气性能 | 体积电阻率 | ASTM D257 | 2.0E 17 | ohm.cm | |
| 介电强度 | ASTM D149 | 430 | V/mil | ||
| 介电常数 | ASTM D150 | 3.0 | |||
| 消耗因数 | ASTM D150 | 0.0010 | |||
| 漏电起痕指数 | ASTM D60112 | 250 | V | ||
| 其他 | 阻燃性 | 0.0197in | UL 94 | V-2 | |
| 0.0630in | UL 94 | V-2 | |||
| 0.0984in | UL 94 | V-2 | |||
| 0.118in | UL 94 | V-2 | |||
| 灼热丝温度 | 0.0787in | ASTM D60695-2-13 | 1560 | ℉ | |
| 氧指数 | ASTM D2863 | 26 | % | ||
| 平均燃烧程度 | ASTM D635 | 1 | in | ||
| 折光率 | ASTM D542 | 1.586 | |||
| 透明度 | ASTM D1003 | 89.0 | % | ||
| 雾度 | ASTM D1003 | 0.70-1.5 | % |
||