| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 885 | g/cm3 | |
| 表面硬度 | JIS K6253 | 87 | shore A | ||
| 熔融指数 | 190℃ | ASTM D1238 | 1.2 | g/10min | |
| 191℃ | ASTM D1239 | 2.2 | g/11min | ||
| 机械性能 | 断裂强度 | JIS K7113 | 27 | Mpa | |
| 断裂伸长 | JIS K7114 | 800 | % | ||
| 扭曲刚性 | ASTM D1043 | 9 | Mpa | ||
热性能 |
熔点 | ASTM D2117 | 66 | ℃ | |
| 维卡软化点 | ASTM D1525 | 58 | ℃ | ||
| 脆化温度 | ASTM D748 | -70 | ℃ | ||
电气性能 |
体积电阻系数 | ASTM D257 | 1017 | Ω-CM | |
| 介电常数 | ASTM D150 | 2.2-2.4 | |||
| 介电正接 | ASTM D150 | 5*10-4 | |||