Fortron 1140L7
聚苯硫醚
40% 玻璃纤维增强材料
Celanese Corporation
产品说明：
One of the easiest flowing 40% glass reinforced grade in the Fortron product line. This material can be processed at fast cycle times due to the unique crystallization characteristics. This product offers good heat and chemical resistance, as well as, good electrical properties. The product is inherently flame-retardant and exhibits high hardness and rigidity.
Fortron 1130L0 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 | |
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 11000 | MPa | ISO 527-2/1A/1 |
| 拉伸应力(断裂) | 160 | MPa | ISO 527-2/1A/5 |
| 拉伸应变(断裂) | 2.0 | % | ISO 527-2/1A/5 |
| 弯曲模量(23°C) | 10400 | MPa | ISO 178 |
| 弯曲应力(23°C) | 255 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m2 | ISO 179/1eA |
| 23°C | 10 | kJ/m2 | ISO 179/1eA |
| 悬壁梁缺口冲击强度(23°C) | 9.5 | kJ/m2 | ISO 180/1A |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度(1.8 MPa, 未退火) | 255 | °C | ISO 75-2/A |
| 玻璃转化温度1 | 90.0 | °C | ISO 11357-2 |
| 熔融温度2 | 280 | °C | ISO 11357-3 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 1.0E 16 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E 18 | ohms·cm | IEC 60093 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级(0.380 mm) | V-0 | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 130 到 140 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 20.0 到 30.0 | °C | |
| 料筒后部温度 | 290 到 300 | °C | |
| 料筒中部温度 | 310 到 320 | °C | |
| 料筒前部温度 | 330 到 340 | °C | |
| 射嘴温度 | 310 到 330 | °C | |
| 加工（熔体）温度 | 330 到 340 | °C | |
| 模具温度 | 140 到 160 | °C | |
| 注塑压力 | 50.0 到 100 | MPa | |
| 注射速度 | 快速 | ||
| 保压 | 30.0 到 70.0 | MPa | |
| 背压 | 0.00 到 3.00 | MPa |