PC 基础创新塑料(美国)243R-111性能项目测试条件测试方法数值/描述单位机械拉伸强度(引张强度) ASTM D638/ISO 52763（70）kg/cm2(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527--%拉伸模量 ASTM D638/ISO 5272350kg/cm2(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 5276.0%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527110%弯曲模量(弯曲弹性率) ASTM D790/ISO 178230000kg/cm2(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 17890000kg/cm2(MPa)[Lb/in2]洛氏硬度 ASTM D785-- IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17970kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 17912.0kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 1791/4，73kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.20 成型收缩率 ASTM D9550.50-0.70%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133300℃.1.2kg,12g/10min220℃/10kgASTM D1238/ISO 1133 g/10min吸水率 23℃/24H ASTM D570/ISO 620.15-0.35%热性能热变形温度退火ASTM D648/ISO 75--℃（℉）未退火ASTM D648/ISO 750.45MPa,100mm,136℃;1.80MPa,100mm,124℃℃（℉）维卡软化点 ASTM D1525/ISO R306141-153℃（℉）熔点 ---℃（℉）燃烧性（率） UL94V2-V0 线性膨胀系数 ASTM D696/ISO 113590.000070mm/mm.℃电气性能介电常数100HZASTM D150/IEC 6025050/60HZ，2.7 1MHZASTM D150/IEC 602502.7 介电损耗100HZASTM D150/IEC 602500.0010 1MHZASTM D150/IEC 602500.010 体积电阻率 ASTM D257/IEC 600931.0E 15 ohm cmΩ.cm表面电阻率 ASTM D257/IEC 60093>1.0E 15 ohmsΩ耐电弧性 ASTM D495/IEC 60112-- 光学性能折射率 ASTM D542/ISO 4891.586 透光率 ASTM D1003/ISO 1346888.0-90.0%模糊系数（Haze） ISO 14782<0.80%加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 Mpa保压压力 Mpa背压 Mpa螺杆转速 rpm其他备注注射成型颜色本色特性加脱模剂、紫外线稳定剂，可加工性良好，中等粘度用途