Global grade. LEXAN LUX2110T is an injection moulding grade especially designed for manufacturing optical parts requiring easy flow properties combined with very high transmission and color stability.

Information provided by SABIC

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D792
Density	1.20 g/cc	0.0434 lb/in3	ASTM D792
Linear Mold Shrinkage, Flow	0.00600 - 0.00900 cm/cm	0.00600 - 0.00900 in/in	SABIC method
Melt Flow	19.0 g/10 min @Load 1.20 kg, Temperature 300 °C	19.0 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	68.0 MPa	9860 psi	50 mm/min; ASTM D638
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ASTM D638
Elongation at Break	143 %	143 %	50 mm/min; ASTM D638

PC LEXAN LUX2110T

主要性能

1．机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；

2．耐热老化性：增强后的UL温度指数达120~140℃（户外长期老化性也很好）；

3．耐溶剂性：无应力开裂；

4．对水稳定性：高温下遇水易分解（高温高湿环境下使用需谨慎）；

5．电气性能：

6．绝缘性能：优良（潮湿、高温也能保持电性能稳定，是制造电子、电气零件的理想材料）；

7．介电系数：3.0—3.2；

8．耐电弧性：120s；

9．成型加工性：普通设备注塑或挤塑。

PC塑料的粘接

根据不同需要，可以选择以下粘合剂：

1．G-933：单组分常温固化软弹性防震粘合剂，耐高低温，不同粘度粘接速度几秒至几个小时固化完毕。

2．KD-833瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PC塑料，但胶层硬脆，不耐60度以上热水浸泡。

3．QN-505，双组分胶，胶层柔软，适合PC塑料大面积粘接或复合。但耐高温性能较差。

4．QN-906：双组分胶，耐高温。

5．G-988：单组份室温硫化胶，固化后是弹性体具有优秀的防水，防震粘合剂，耐高低温， 1—2mm厚度的话，10分钟左右初固，5—6小时基本固化，有一定的强度。完全固化的话需要至少24小时。单组份，不需要混合，挤出后涂抹静置即可，无需加温。

6．KD-5606：UV紫外线固化胶，粘合透明PS片材及板材，可达无痕迹效果，需要用紫外线灯照射固化。粘后效果美观。但耐高温性能较差。

用途

光学照明

用于制造大型灯罩、防护玻璃、光学仪器的左右目镜筒等，还可广泛用于飞机上的透明材料。

电子电器

聚碳酸酯是优良的E（120℃）级绝缘材料，用于制造绝缘接插件、线圈框架、管座、绝缘套管、电话机壳体及零件、矿灯的电池壳等。也可用于制作尺寸精度很高的零件，如光盘、电话、电子计算机、视频录象机、电话交换器、信号继电器等通讯器材。聚碳酸酯薄摸还被广泛用作电容器、绝缘皮包、录音带、彩色录象磁带等。

机械设备

用于制造各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮，也可作一些机械设备壳体、罩盖和框架等零件。

医疗器材

可作医疗用途的杯、筒、瓶以及牙科器械、药品容器和手术器械，甚至还可用作人工肾、人工肺等人工脏器。

其它方面

建筑上用作中空筋双壁板、暖房玻璃等；在纺织行业用作纺织纱管、纺织机轴瓦等；日用方面作奶瓶、餐具、玩具、模型、LED灯外壳和手机外壳等。

PC LEXAN LUX2110T 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！