Asaflex 805
苯乙烯-丁二烯-苯乙烯嵌段共聚物
AKelastomers
产品说明:
Injection molding grade. For molded products with superior balance of high-level impact strength and rigidity, maximum transparency, and good surface appearance. It is supplied in pellet form.
Food containers, cosmetics caps, pencil cases and other stationery goods, toys, swim goggle and other cases, consumer goods
Asaflex 805 物性表
Injection molding grade. For molded products with superior balance of high-level impact strength and rigidity, maximum transparency, and good surface appearance. It is supplied in pellet form.
Food containers, cosmetics caps, pencil cases and other stationery goods, toys, swim goggle and other cases, consumer goods
Food containers, cosmetics caps, pencil cases and other stationery goods, toys, swim goggle and other cases, consumer goods
基本信息 | |
---|---|
特性 |
|
用途 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.02 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率) (200°C/5.0 kg) | 10 | g/10 min | ISO 1133 |
收缩率 | 0.20 到 0.80 | % | |
吸水率 (23°C, 24 hr) | < 0.10 | % | ISO 62 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
洛氏硬度 (R 计秤) | 88 | ISO 2039-2 | |
肖氏硬度 (邵氏 D) | 75 | ISO 868 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸应力 (屈服) | 30.0 | MPa | ISO 527-2/5 |
拉伸应变 (断裂) | 15 | % | ISO 527-2/5 |
弯曲模量 | 1550 | MPa | ISO 178 |
弯曲应力 | 50.0 | MPa | ISO 178 |
Due to good compatibility with styrenic resins such as GPPS, Asaflex? can be blended at arbitrary ratio.
Grade | MFR*1 | Flexural Modulus |
Vicat Softening Point*2 |
Haze*3 | Applications |
---|---|---|---|---|---|
800S | 6 | 2250 | 96 | 3.0 | Food PackagingMedicalTransparent Molded Products |
805 | 10 | 1550 | 91 | 0.5 | FootwearMedicalTransparent Molded Products |
810 | 5 | 1400 | 83 | 1.2 | Polymer ModificationAdhesives and SealantsFootwearTransparent Molded Products |
815 | 6 | 1200 | 82 | 0.5 | Food PackagingPolymer Modification |
825 | 6 | 1200 | 82 | 0.5 | Polymer ModificationFootwearTransparent Molded Products |
830 | 6 | 1100 | 72 | 2.0 | Polymer ModificationTransparent Molded Products |
835 | 6 | 1100 | 72 | 2.0 | Food PackagingPolymer Modification |
840 | 7 | 1500 | 81 | 1.2 | Polymer ModificationTransparent Molded Products |
845 | 7 | 1500 | 81 | 1.2 | Food PackagingPolymer Modification |
*1 200°C, 5kgf
*2 10 N Load, 50 K/h
*3 2mm Thick Plate