Asaflex 815
苯乙烯-丁二烯-苯乙烯嵌段共聚物
AKelastomers
产品说明：
Sheet grade. Blended with SC*, for highly transparent sheets. It is supplied in pellet form.
Blended with SC* for transparent blister packs and other sheets, with GPPS for frozen dessert cups and other containers, and with GPPS/Tufprene? to obtain PS sheets for food containers and other applications.
* Styrenic copolymer from PS Japan Corp. similar to Asaflex? 815 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS (general-purpose polystyrene).
Asaflex? 815 物性表
Sheet grade. Blended with SC*, for highly transparent sheets. It is supplied in pellet form.
Blended with SC* for transparent blister packs and other sheets, with GPPS for frozen dessert cups and other containers, and with GPPS/Tufprene? to obtain PS sheets for food containers and other applications.
* Styrenic copolymer from PS Japan Corp. similar to Asaflex? 815 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS (general-purpose polystyrene).
Blended with SC* for transparent blister packs and other sheets, with GPPS for frozen dessert cups and other containers, and with GPPS/Tufprene? to obtain PS sheets for food containers and other applications.
* Styrenic copolymer from PS Japan Corp. similar to Asaflex? 815 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS (general-purpose polystyrene).
Asaflex? 815 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (200°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| 收缩率 | 0.20 到 0.80 | % | |
| 吸水率 (23°C, 24 hr) | 0.10 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 计秤) | 55 | ISO 2039-2 | |
| 肖氏硬度 (邵氏 D) | 71 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 (屈服) | 27.0 | MPa | ISO 527-2/5 |
| 拉伸应变 (断裂) | 200 | % | ISO 527-2/5 |
| 弯曲模量 | 1200 | MPa | ISO 178 |
| 弯曲应力 | 37.0 | MPa | ISO 178 |
Due to good compatibility with styrenic resins such as GPPS, Asaflex? can be blended at arbitrary ratio.
| Grade | MFR*1 | Flexural Modulus |
Vicat Softening Point*2 |
Haze*3 | Applications |
|---|---|---|---|---|---|
| 800S | 6 | 2250 | 96 | 3.0 | Food PackagingMedicalTransparent Molded Products |
| 805 | 10 | 1550 | 91 | 0.5 | FootwearMedicalTransparent Molded Products |
| 810 | 5 | 1400 | 83 | 1.2 | Polymer ModificationAdhesives and SealantsFootwearTransparent Molded Products |
| 815 | 6 | 1200 | 82 | 0.5 | Food PackagingPolymer Modification |
| 825 | 6 | 1200 | 82 | 0.5 | Polymer ModificationFootwearTransparent Molded Products |
| 830 | 6 | 1100 | 72 | 2.0 | Polymer ModificationTransparent Molded Products |
| 835 | 6 | 1100 | 72 | 2.0 | Food PackagingPolymer Modification |
| 840 | 7 | 1500 | 81 | 1.2 | Polymer ModificationTransparent Molded Products |
| 845 | 7 | 1500 | 81 | 1.2 | Food PackagingPolymer Modification |
*1 200°C, 5kgf
*2 10 N Load, 50 K/h
*3 2mm Thick Plate