东莞市恒磊塑胶有限公司
PC LUPOY 1303-15
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Agency Ratings
|
|
|||
|
RoHS Compliance
|
|
|||
|
Automotive Specifications
|
|
|||
|
UL File Number
|
|
|||
|
Appearance
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow
|
|
in/in
|
ASTM D955 |
|
Water Absorption
|
ASTM D570 | ||
|
24 hr, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|
psi
|
ASTM D638 |
|
Tensile Strength
|
ASTM D638 | ||
|
Yield
|
|
psi
|
|
|
Break
|
|
psi
|
|
|
Tensile Elongation
|
ASTM D638 |
PC LUPOY 1303-15
塑料的处理
PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。
注塑机选用
PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。
主要优点
1．具高强度及弹性系数、高冲击强度、使用温度范围广；
2．高度透明性及自由染色性；
3．成形收缩率低、尺寸安定性良好；
4．耐疲劳性佳；
5．耐候性佳；
6．电气特性优。
性能特点:良好的流动性;脱模性能良好;
粘度，高；光学透明性好、抗冲击强度高；
并具有优异的热安稳性、耐蠕变性、抗寒性、电绝缘性和阻燃性等。
加工方法:薄膜挤出；吹塑成型；挤出成型；热成型；树脂传递成型；涂层；砑光；注射成型也是最重要的加工方法之一；
用途:在透明建筑板材、电子电器、光盘、汽车工业、机械、光学、医药等领域得到广泛运用。
PC塑料物理性能以及加工
低温-45度聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通运用温度内都有出色的机械功用。