INFINO LS-1159S

Technical Datasheet | Supplied by LOTTE Advanced Materials

INFINO? LS-1159S by LOTTE Advanced Materials is a halogen-free, flame retarded polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy reinforced with 15 % glass fiber. Exhibits high impact strength & modulus, high flowability, good colorability, excellent appearance and well-balanced mechanical properties & processability. Can be processed using injection molding. INFINO? LS-1159S is recommended for electronic application such as television.

Physical Properties	Metric	English	Comments
Specific Gravity	1.28 g/cc	1.28 g/cc	Natural or representative color; ASTM D792
Linear Mold Shrinkage, Flow	0.0010 cm/cm @Thickness 3.20 mm	0.0010 in/in @Thickness 0.126 in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0010 cm/cm @Thickness 3.20 mm	0.0010 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 250 °C	9.0 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238
	25 g/10 min @Load 10.0 kg, Temperature 220 °C	25 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238
Ash	14 %	14 %	ASTM D5630
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength at Break	88.3 MPa	12800 psi	5 mm/min; ASTM D638
Tensile Strength, Yield	88.3 MPa	12800 psi	5 mm/min; ASTM D638

PC/ABS INFINO LS-1159S

简介

ABS工程塑料即PC+ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC+ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。ABS工程塑料最大的缺点就是质量重、导热性能欠佳。它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。

PC/ABS应用

1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件

2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器

3.电信，移动电话外壳，附件以及智能卡（SIM卡）：

4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道

5.家用电器，如洗衣机，吹风机，微波炉内外部件

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。

PC/ABS INFINO LS-1159S 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！