EVA LD319.92物性
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.930 | g/cm3; |
|
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 2.0 | g/10 min |
|
| 醋酸乙烯含量 | ExxonMobil Method | 8.7 | wt |
||
| 机械性能 | 割线模量 | 1 正割, MD | ASTM D882 | 108 | MPa |
1 正割, TD |
ASTM D882 | 120 | MPa |
||
| 抗张强度 | MD: 断裂 |
ASTM D882 | 30.5 | MPa |
|
TD: 断裂 |
ASTM D882 | 27.4 | MPa |
||
| 伸长率 | MD: 断裂 |
ASTM D882 | 330 | ||
TD: 断裂 |
ASTM D882 | 660 | |||
| 落锤冲击 | ASTM D1709A | 250 | g | ||
| 埃尔曼多夫抗撕强度 | MD |
ASTM D1922 | 120 | g | |
TD |
ASTM D1922 | 95 | g | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 81.0 | °C |
|