TPEE HYTREL HTR8241
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | ISO 1183 |
| Melt Density | 1.07 g/cc @Temperature >=211 °C |
0.0387 lb/in3 @Temperature >=412 °F |
|
| Water Absorption | 0.70 % @Thickness 2.00 mm |
0.70 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Moisture Absorption | 0.200 % @Thickness 2.00 mm |
0.200 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | ISO 294-4, 2577 |
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR and melt density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ISO 7619-1 |
| 60 @Time 15.0 sec |
60 @Time 0.00417 hour |
ISO 7619-1 | |
TPEE HYTREL HTR8241
TPEE性能：
热性能
TPEE具有优异的耐热性能，硬度越高，耐热性越好；TPEE在110～140℃连续加热10h基本不失重，在160℃和180℃分别加热10h，失重仅为0.05%和0.1%，因而TPEE的使用温度非常高，短期使用温度更高，能适应汽车生产线上的烘漆温度(150～160℃)，并且它在高低温下机械性能损失小。TPEE在120℃以上使用，其拉伸强度远远高于TPU此外TPEE还具有出色的耐低温性能，TPEE脆点低于-70℃并且硬度越低，耐寒性越好，大部分TPEE可在-40℃下长期使用。
耐化学介质性
TPEE具有极佳的耐油性，在室温下能耐大多数极性液体化学介质(如酸、碱、胺二醇类化合物)，但对卤代烃(氟里昂除外)及酚类的作用却无能为力，其耐化学品的能力随其硬度的提高而提高。TPEE对大多数有机溶剂、燃料及气体的抗溶胀性能和抗渗透性能是好的，对燃油渗透性仅为氯丁胶、氯磺化聚乙烯、丁腈胶等耐油橡胶的1/3～1/300但TPEE耐热水性较差，添加聚碳酰亚胺稳定剂可以明显改善其抗水解性能。
耐老化性
TPEE在很多不同条件下，如在水雾、臭氧、室外大气老化等条件下，化学稳定性优良。象大多数弹性体一样，在紫外光作用下会发生降解，因此对于室外应用或制品受阳光照射的条件，配方中应添加紫外光防护助剂，其中包括炭黑和各种颜料或其它屏蔽材料;此外TPEE还具有不同程度的水解性。
TPEE应用
TPEE主要用于要求减震、耐冲击、耐曲挠、密封性和弹性、耐油、耐化学品并要求足够强度的领域。如：聚合物改性、汽车部件、耐高低温电线护套、液压软管、鞋材、传动皮带、旋转成型轮胎、挠性连轴节、消音齿轮、电梯滑道、化工设备管道阀件中的防腐耐磨耐高低温材料等。TPEE高性能的产品牌号有美国杜邦公司的TPEE 5526,5556，4056，4069等，广泛用于电线电缆以及密封件等。