PBT VALOX 310 

Physical Properties	Metric	English	Comments
Specific Gravity	1.31 g/cc	1.31 g/cc	ASTM D792
	1.31 g/cc	1.31 g/cc	ASTM D792
Water Absorption	0.0800 %	0.0800 %	24 hours; ASTM D570
Viscosity	600000 cP	600000 cP	melt; SABIC method
Linear Mold Shrinkage, Flow	0.00900 - 0.0160 cm/cm @Thickness 0.750 - 2.30 mm	0.00900 - 0.0160 in/in @Thickness 0.0295 - 0.0906 in	SABIC method
	0.0150 - 0.0230 cm/cm @Thickness 2.30 - 4.60 mm	0.0150 - 0.0230 in/in @Thickness 0.0906 - 0.181 in	SABIC method
Linear Mold Shrinkage, Transverse	0.0100 - 0.0170 cm/cm @Thickness 0.750 - 2.30 mm	0.0100 - 0.0170 in/in @Thickness 0.0295 - 0.0906 in	SABIC method
	0.0160 - 0.0240 cm/cm @Thickness 2.30 - 4.60 mm	0.0160 - 0.0240 in/in @Thickness 0.0906 - 0.181 in	SABIC method
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	117	117	ASTM D785
Tensile Strength at Break	51.0 MPa	7400 psi	50 mm/min; ASTM D638
Tensile Strength, Yield	51.0 MPa	7400 psi	50 mm/min; ASTM D638
Elongation at Break	300 %	300 %	50 mm/min; ASTM D638
Flexural Strength	82.0 MPa	11900 psi	brk, 1.3 mm/min, 50 mm span; ASTM D790

PBT VALOX 310 

特性

PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。PBT吸湿特性很弱。非增强型PBT的张力强度为50MPa，玻璃添加剂型的PBT张力强度为170MPa。玻璃添加剂过多将导致材料变脆。PBT的结晶很迅速，这将导致因冷却不均匀而造成弯曲变形。对于有玻璃添加剂类型的材料，流程方向的收缩率可以减小，但与流程垂直方向的收缩率基本上和普通材料没有区别。一般材料收缩率在1.5%~2.8%之间。含30%玻璃添加剂的材料收缩0.3%~1.6%之间。熔点（225℃）和高温变形温度都比PET材料要低。维卡软化温度大约为170℃。玻璃化转换温度（glass trasitio temperature）在22℃到43℃之间。由于PBT的结晶速度很高，因此它的粘性很低，塑件加工的周期时间一般也较低。

三、PBT塑料的粘接：

　　根据不同需要，可以选择以下粘合剂：

　　1. TG-3200：单组分常温固化软弹性防震粘合剂，耐高低温，但粘接速度慢，胶水通常要1天或几天时间才能固化完毕。

　　2. TS-8602瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PBT，但胶层硬脆，不耐水。

　　3. TE-9270类，双组分胶，胶层柔软，适合PBT大面积粘接或复合。但耐高温性能较差。

　　4.TE-9249类胶：双组分胶，耐高温。

应用范围

家用器具（食品加工刀片、真空吸尘器元件、电风扇、头发干燥机壳体、咖啡器皿等），电器元件（开关、电机壳、保险丝盒、计算机键盘按键等），汽车工业（散热器格窗、车身嵌板、车轮盖、门窗部件等）。

PBT VALOX 310 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！