东莞市腾烁化工有限公司
产品描述
| 颜色 | |
| 特性 | 耐高温;抗化学性;透明 |
| 用途 | 电器用具;汽车内部零件;汽车外部零件 |
LG Chemical 82TR SAN, High Transparency, Heat Resistance, Chemical Resistance 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| 处理 | 0.010 | 0.010 | Injection Molding |
| 线性成型收缩率,Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| 熔体流动速率 | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 18 g/10 min @Load 3.80 kg, Temperature 230 °C |
18 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 | |
| 53 g/10 min @Load 10.0 kg, Temperature 220 °C |
53 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 124 | 124 | ASTM D785 |
| 抗张强度(屈服) | 66.7 MPa @Thickness 3.20 mm |
9670 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| 伸长率 (断裂) | 6.0 % @Thickness 3.20 mm |
6.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| 拉伸模量 | 3.08 GPa @Thickness 3.20 mm |
447 ksi @Thickness 0.126 in |
1 mm/min; ASTM D638 |
| 弯曲强度 | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| 弯曲模量 | 3.60 GPa @Thickness 3.20 mm |
522 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.0981 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
0.184 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 0.0981 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
0.184 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| 介电强度 | 29.0 kV/mm | 737 kV/in | |
| 耐电弧性 | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | |
| 热丝引燃 (HWI) | 7.0 - 15 sec @Thickness >=1.50 mm |
7.0 - 15 sec @Thickness >=0.0591 in |
|
| 15 - 30 sec @Thickness >=3.00 mm |
15 - 30 sec @Thickness >=0.118 in |
||
| 高电弧燃烧指数(HAI) | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
|
| >= 120 arcs @Thickness 3.00 mm |
>= 120 arcs @Thickness 0.118 in |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | >= 90.0 °C @Thickness 6.40 mm |
>= 194 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| 维卡软化温度 | 101 °C @Load 5.00 kg |
214 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
| UL RTI | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| UL RTI，机械冲击 | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| UL RTI，机械无冲击 | 50.0 °C @Thickness <=1.50 mm |
122 °F @Thickness <=0.0591 in |
|
| 50.0 °C @Thickness <=3.00 mm |
122 °F @Thickness <=0.118 in |
||
| 可燃性(UL94) | HB @Thickness >=1.60 mm |
HB @Thickness >=0.0630 in |
|
| HB @Thickness >=3.20 mm |
HB @Thickness >=0.126 in |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| 料筒中部温度 | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| 料筒前部温度 | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| 射嘴温度 | 190 - 220 °C | 374 - 428 °F | Injection Molding |
| 加工（熔体）温度 | 190 - 220 °C | 374 - 428 °F | Injection Molding |
| 模具温度 | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| 干燥温度 | 80.0 °C | 176 °F | Injection Molding |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| 背压 | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| 螺杆转速 | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |