PPO 沙伯基础 PX9406 阻燃级 高抗冲 高耐热聚苯醚
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.09 | |||
| 吸水率 | 24hrs | ASTM D570 | 0.06 | % | ||
| 模具收缩率 | 3.2mm | ASTM D955 | 5-7 | E-3 | ||
| 机械性能 | 拉伸强度 | 3.2mm | ASTM D638 | 75 | MPa | |
| 断裂拉伸率 | 3.2mm | ASTM D638 | 18 | % | ||
| 弯曲强度 | 6.4mm | ASTM D790 | 112 | MPa | ||
| 弯曲模量 | 6.4mm | ASTM D790 | 2646 | MPa | ||
| 缺口冲击强度 | 23℃ | ASTM D256 | 160 | J/M | ||
| 电气性能 | 损耗因数 | 60Hz | ASTM D150 | - | - | |
| 介电常数 | 1MHz | ASTM D150 | 2.49 | |||
| 体积电阻 | ASTM D257 | 2.0E 16 | ohm·cm | |||
| 表面电阻 | D257 | 1.0E 16 | ohm·cm | |||
| 热性能 | 热变形温度 | 0.45MPa | ASTM D648 | 133 | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D648 | 125 | ℃ | ||
| 维卡软化点 | ASTM D1525 | 150 | ℃ | |||
| UL长期使用温度 | 电气 | UL746B | 105 | ℃ | ||
| 含冲击 | UL746B | 100 | ℃ | |||
| 无冲击 | UL746B | 105 | ℃ | |||
| 阻燃性 | UL94 | V-0 |
||||