TPEE/美国杜邦/HTR8068原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 24小时吸水率 | ASTM D-570 | 1.9 | % | ||
| 物理性能 | 泰伯磨耗量 | CS-17轮 | 25 | mg/1000rev | ||
| 熔体流动速率 | ASTM D-1238 | 4.6 | g/10min | |||
| 熔体流动速率 | ASTM D-3418 | 190 | g/10min | |||
| 比重 | ASTM D-792 | 1.43 | ||||
| 机械性能 | 拉伸力 | 5%伸长 | ASTM D-638 | 3.9 | MPa | |
| 10%伸长 | ASTM D-638 | 5.2 | MPa | |||
| 初耐撕裂性能 | ASTM D-1004 | 75 | kn/m | |||
| 断裂拉伸力 | ASTM D-638 | 12.4 | MPa | |||
| 揉曲模量 | ASTM D-790 | 174 | MPa | |||
| 硬度计硬度 | ASTM D-2240 | 46 | ||||
| 断裂伸长 | ASTM D-638 | 340 | % | |||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 不破裂 | J/M | ||
| 热性能 | 热畸变温度 | @0.18MPa | ASTM D-648 | -- | ℃ | |
| 热畸变温度 | @0.5MPa | ASTM D-648 | -- | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 110 | ℃ | |||
| 熔点 | ASTM D-3418 | 169 | ℃ | |||
| 其它性能 | 耐揉曲切口增长性能 | ASTM D-1052 | -- | |||