PA66 Zytel 70G25HSLR NC010

25% Glass Reinforced, Heat Stabilized, Hydrolysis Resistant, Polyamide 66

Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/in3	DAM; ISO 1183
Melt Density	1.15 g/cc @Temperature >=262 °C	0.0415 lb/in3 @Temperature >=504 °F
Water Absorption	6.4 % @Thickness 2.00 mm	6.4 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	2.00 % @Thickness 2.00 mm	2.00 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Number	150 cm3/g	1.50 dl/g	DAM; ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	DAM; ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	DAM; ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	260 MPa	37700 psi	H 961/30; ISO 2039-1
Tensile Strength at Break	120 MPa	17400 psi	50% RH; ISO 527-1/-2
	180 MPa	26100 psi	DAM; ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	DAM; ISO 527-1/-2
	7.0 %	7.0 %	50% RH; ISO 527-1/-2
Tensile Modulus	6.00 GPa	870 ksi	50% RH; ISO 527-1/-2
	8.50 GPa	1230 ksi	DAM; ISO 527-1/-2
Flexural Strength	170 MPa	24700 psi	50% RH; ISO 178
	260 MPa	37700 psi	DAM; ISO 178

PA66 Zytel 70G25HSLR NC010

PA特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

PA66应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等

PA66 Zytel 70G25HSLR NC010 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！