产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 吸水率 | 24hr,in 23℃ | ASTM D-570 | 0.20 | % | |
物理性能 | 比重 | ASTM D-792 | 1.20 | |||
阻燃性 | 厚度1.47mm | UL 94 | 94V-2 | |||
透光率 | 厚度3mm | ASTM D-1003 | 88 | % | ||
折射率 | ASTM D-542 | 1.585 | ||||
阻燃性 | 厚度3.05mm | UL 94 | 94V-2 | |||
机械性能 | 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 830(85) | j/m(kgf.cm/cm) | |
弯曲强度 | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | |||
拉伸率 | 屈服点 | ASTM D-638 | 6 | |||
断裂点 | ASTM D-638 | 140 | ||||
拉伸强度 | 屈服点 | ASTM D-638 | 62(630) | Mpa(kgf/cm2) | ||
断裂点 | ASTM D-638 | 78(800) | Mpa(kgf/cm2) | |||
洛氏硬度 | ASTM D-785 | 77 | 洛氏硬度 | |||
耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 130(13) | j/m(kgf.cm/cm) | ||
弯曲模量 | ASTM D-792 | 2260(23000) | Mpa(kgf/cm2) | |||
拉伸模量 | ASTM D-638 | 2130(21700) | Mpa(kgf/cm2) | |||
压缩强度 | ASTM D-695 | 76(780) | Mpa(kgf/cm2) | |||
电气性能 | 体积电阻率 | ASTM D-257 | 3 | 1016Ω.cm | ||
耐导电径迹性(CTI) | IEC 112 | 300 | V | |||
介电率 | 106Hz | ASTM D-150 | 2.9 | |||
介电率 | 60Hz | ASTM D-150 | 2.95 | |||
介电正切 | 106Hz | ASTM D-150 | 0.009 | |||
耐电弧性 | ASTM D-495 | 110 | sec | |||
介电正切 | 60Hz | ASTM D-150 | 0.0004 | |||
绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm | ||
加工性能 | 成型收缩率 | 流动方向 | ASTM D-955 | 0.5~0.7 | % | |
垂直方向 | ASTM D-955 | 0.5~0.7 | % | |||
热性能 | 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 142 | °C | |
线膨胀系数 | 流动方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | ||
垂直方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | |||
负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 132 | °C | ||
温度指数 | 电学式 | 厚度1.47mm | UL 746B | 125 | °C | |
冲击式 | 厚度1.47mm | UL 746B | 115 | °C | ||
非冲击式 | 厚度1.47mm | UL 746B | 125 | °C |