DuPont? Entira? AS MK400 产品信息：
| 工艺大全 | |
|---|---|
| 添加剂 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.970 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238, ISO 1133 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 58.9 | °C | ASTM D1525, ISO 306 |
| 溶融温度（DSC） | 91.1 | °C | ASTM D3418, ISO 3146 |
| Freezing Point - (DSC) | 61 | °C | ASTM D3418 |
| 补充信息 | 额定值 | 单位制 | |
|---|---|---|---|
| Processing Temperature - Maximum | 250 | °C | |
| General Processing Information: Entira? AS MK400 is a very hygroscopic material. To minimize exposure to moisture, any remaining material should be hermetically sealed in a barrier package immediately after use. The bag have as much air removed as possible prior to sealing. A vacuum to pull out the air can be used to assist this process. In order to reuse remaining material that has been hermetically sealed, the material should be dried under vacuum with a nitrogen flow at 50-60°C for several hours prior to use. Entira? AS MK400 is available in pellet form for use in conventional equipment for processing polyolefins. Entira? AS MK400 can be fed together with base polymers and other additives in the hopper during processing. Typical addition levels range from 10 - 30%. |