| 性能项目 | 测试方法 | 测试条件 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.30 | g/cm3 | |
| 熔体流动速率 | ASTM D1238 | 14 | g/10min | ||
| 成型收缩率 | ASTM D955 | 流动m | 0.7 | % | |
| 吸水率 | ASTM D570 | 24hr | 0.37 | % | |
| 机械性能 | 拉伸模量 | ASTM D638 | 2340 | MPa | |
| 拉伸强度 | ASTM D638 | 屈服 | 69.6 | MPa | |
| 拉伸强度 | ASTM D638 | 断裂 | 69.6 | MPa | |
| 拉伸伸长率 | ASTM D638 | 屈服 | 7.2 | % | |
| 拉伸伸长率 | ASTM D638 | 断裂 | 60 | % | |
| 弯曲模量 | ASTM D790 | 2410 | MPa | ||
| 弯曲强度 | ASTM D790 | 屈服 | 91 | MPa | |
| 压缩模量 | ASTM D695 | 1730 | MPa | ||
| 压缩模量 | ASTM D695 | 98.9 | MPa | ||
| 鞘强度 | ASTM D732 | 62.7 | MPa | ||
| 泊松比 | ASTM E132 | 0.42 | |||
| IZOD缺口冲击强度 | ASTM D256 | 694 | J/m | ||
| IZOD无缺口冲击强度 | ASTM D256 | 不断裂 | J/m | ||
| 拉伸冲击强度 | ASTM D1822 | 399 | KJ/m2 | ||
| 热性能 | 热变形温度 | ASTM D648 | 1.8MPa，未退火 | 207 | ℃ |
| 热变形温度 | ASTM D648 | 0.45MPa，未退火 | 214 | ℃ | |
| 玻璃转化温度 | ASTM E1356 | 220 | ℃ | ||
| 线形膨胀系数 | ASTM D696 | 0.000056 | cm/cm/℃ | ||
| 导热系数 | ASTM C177 | 0.35 | W/m/K | ||
| 阻燃性 | UL 94 | 1.57mm | V-0 | ||
| 氧指数 | ASTM D2863 | 38 | % | ||
| 电气性能 | 体积电阻率 | ASTM D257 | 9.0E 15 | ohm.cm | |
| 介电强度 | ASTM D149 | 14 | kV/mm | ||
| 介电常数 | ASTM D150 | 60Hz | 3.44 | ||
| 介电常数 | ASTM D150 | 1kHz | 3.40 | ||
| 光学性能 | 折射率 | ASTM D542 | 1.672 | ||
PPSU为略带琥珀色的线型聚合物。对一般酸、碱、盐、醇、脂肪烃等稳定。部分溶于酯酮`芳烃,可溶于卤烃`DM。刚性和韧性好，耐温、耐热氧化，抗蠕变性能优良，耐无机酸、碱、盐溶液的腐蚀，耐离子辐射，无毒，绝缘性和自熄性好，容易成型加工。