LNP? LUBRICOMP? KL004 compound
聚甲醛（POM）共聚物
产品说明：
LNP LUBRICOMP* KL004 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP Fulton* Tradename.
Also known as: LNP* LUBRICOMP* Compound 404
Product reorder name: KL004
LNP? LUBRICOMP? KL004 compound 物性表
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.50 |
g/cm3 |
ASTM D792, ISO 1183 |
| 收缩率 |
|
|
|
| 流动 : 24小时 |
2.0 到 2.5 |
% |
ASTM D955 |
| 横向流动 : 24小时 |
2.0 到 2.5 |
% |
ASTM D955 |
| 垂直流动方向 : 24小时 |
2.0 到 2.5 |
% |
ISO 294-4 |
| 流动方向 : 24小时 |
2.0 到 2.5 |
% |
ISO 294-4 |
| 吸水率 |
|
|
|
| 24 hr, 50% RH |
0.15 |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
0.26 |
% |
ISO 62 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| -- 1 |
2140 |
MPa |
ASTM D638 |
| -- |
2400 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 |
51.1 |
MPa |
ASTM D638 |
| 屈服 |
47.3 |
MPa |
ISO 527-2 |
| 断裂 |
50.9 |
MPa |
ASTM D638 |
| 断裂 |
46.5 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
| 屈服 |
11 |
% |
ASTM D638 |
| 屈服 |
10 |
% |
ISO 527-2 |
| 断裂 |
18 |
% |
ASTM D638 |
| 断裂 |
23 |
% |
ISO 527-2 |
| 弯曲模量 |
|
|
|
| -- |
2070 |
MPa |
ASTM D790 |
| -- |
2600 |
MPa |
ISO 178 |
| 弯曲强度 |
|
|
|
| -- |
75.8 |
MPa |
ASTM D790 |
| -- |
79.3 |
MPa |
ISO 178 |
| 摩擦系数 |
|
|
ASTM D3702 Modified |
| 与自身 - 动态 |
0.29 |
|
ASTM D3702 Modified |
| 与自身 - 静态 |
0.15 |
|
ASTM D3702 Modified |
| 磨损因数 - Washer |
15.0 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
|
| 23°C |
43 |
J/m |
ASTM D256 |
| 23°C 2 |
4.0 |
kJ/m2 |
ISO 180/1A |
| 无缺口悬臂梁冲击 |
|
|
|
| 23°C |
640 |
J/m |
ASTM D4812 |
| 23°C 3 |
45 |
kJ/m2 |
ISO 180/1U |
| 装有测量仪表的落镖冲击 |
|
|
|
| 23°C, Energy at Peak Load |
6.40 |
J |
ASTM D3763 |
| -- |
0.770 |
J |
ISO 6603-2 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火, 3.20 mm |
157 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm |
99.4 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 4 |
98.0 |
°C |
ISO 75-2/Af |
| 线形热膨胀系数 |
|
|
ASTM E831, ISO 11359-2 |
| 流动 : -40 到 40°C |
1.1E-4 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 横向 : -40 到 40°C |
1.1E-4 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
82.2 |
°C |
|
| 干燥时间 |
4.0 |
hr |
|
| 料筒后部温度 |
177 到 188 |
°C |
|
| 料筒中部温度 |
193 到 204 |
°C |
|
| 料筒前部温度 |
210 到 221 |
°C |
|
| 加工（熔体）温度 |
199 到 216 |
°C |
|
| 模具温度 |
82.2 到 110 |
°C |
|
| 背压 |
0.172 到 0.344 |
MPa |
|
| 螺杆转速 |
30 到 60 |
rpm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
80*10*4 |
| 3 . |
80*10*4 |
| 4 . |
80*10*4 mm |