POM | 聚甲醛#赛钢
美国杜邦
577 物性表
| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 密度 | 1.56 | ASTM D-792 |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 吸水量 | ASTM D-570 | ||
| (24hrs浸泡+73℉(+23℃)) | 0.25 | % | |
| (Equil.50%R.h.+73℉(+23℃)) | 0.20 | % | |
| (浸泡均衡点+73℉(+23℃)) | 1.00 | % |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 挠曲系数 (+212℉) | 300 | MPsi | 在25℃下 |
| 压缩应力 (+73℉@10%ASTM D-ef.) | 18.0 | MPsi | ASTM D-695 |
| 伸张强度 (+23℃) | 58.6 | MPa | ASTM D-638 |
| 弯曲疲劳忍耐限度 (+73℉) | 4.5 | MPsi | ASTM D-671 |
| 洛氏硬度 | M90,R118 | ASTM D-785 | |
| 挠曲系数 | 在25℃下 | ||
| (+70℃) | 3795 | MPa | |
| (+250℉) | 270 | MPsi | |
| 伸张强度 (+122℃) | 20.7 | MPa | ASTM D-638 |
| 断裂时之拉力伸张度 (+73℉(+23℃)) | 12 | % | ASTM D-638 |
| 负载下之变形 (2000psi@+122℉(14Mpa@50℃)) | 0.4 | % | ASTM D-621 |
| 挠曲系数 | 在25℃下 | ||
| (+100℃) | 2480 | MPa | |
| (+23℃) | 5030 | MPa | |
| 弯曲降服强度 (+73℉) | 10.7 | MPsi | ASTM D-790 |
| 剪力 (+23℃) | 65.5 | MPa | ASTM D-732 |
| 挠曲系数 (+122℃) | 1860 | MPa | 在25℃下 |
| 拉力冲击抵抗力 (+73℉) | 33 | ft.lb/in | ASTM D-1822 |
| 弹性系数 (+23℃) | 6200 | MPa | ASTM D-638 |
| 伸张强度 | ASTM D-638 | ||
| (-55℃) | 88.0 | MPa | |
| (+212℉) | 4.1 | MPsi | |
| (+250℉) | 3.0 | MPsi | |
| 压缩应力 (+73℉@1%ASTM D-ef.) | 5.2 | MPsi | ASTM D-695 |
| 挠曲系数 (+73℉) | 730 | MPsi | 在25℃下 |
| 断裂时之拉力伸张度 (+212℉(+100℃)) | >260 | % | ASTM D-638 |
| 拉力冲击抵抗力 (+23℃) | 67 | kj/m | ASTM D-1822 |
| 剪力 (+73℉) | 9.5 | MPsi | ASTM D-732 |
| 伸张强度 (-68℉) | 12.7 | MPsi | ASTM D-638 |
| 断裂时之拉力伸张度 (+158℉(+70℃)) | 50 | % | ASTM D-638 |
| 摩擦系数 (+73℉(+23℃)动态) | 0.35 | ThrustWasherTest | |
| 绝缘强度 (Short Time,2.3mm) | 19.3(3.2mm) | MV/m | |
| 弹性系数 (+73℉) | 900 | MPsi | ASTM D-638 |
| 伸张强度 (+158℉) | 5.8 | MPsi | ASTM D-638 |
| 断裂时之拉力伸张度 (-68℉(-55℃)) | 3 | % | ASTM D-638 |
| 挠曲系数 (-68℉) | 930 | MPsi | 在25℃下 |
| IZOD冲击强度 (-40℉) | 0.5 | ft.lb/in | ASTM D-256 |
| 挠曲系数 | 在25℃下 | ||
| (+158℉) | 550 | MPsi | |
| (-55℃) | 6410 | MPa | |
| 伸张强度 (+70℃) | 40.0 | MPa | ASTM D-638 |
| IZOD冲击强度 (+23℃) | 42.7 | j/m | ASTM D-256 |
| 伸张强度 (+73℉) | 8.5 | MPsi | ASTM D-638 |
| 压缩应力 (+23℃@1%ASTM D-ef.) | 36.0 | MPa | ASTM D-695 |
| IZOD冲击强度 (40℃) | 26.7 | j/m | ASTM D-256 |
| 压缩应力 (+23℃@10%ASTM D-ef.) | 124 | MPa | ASTM D-695 |
| 伸张强度 (+100℃) | 28.3 | MPa | ASTM D-638 |
| 弯曲降服强度 (+23℃) | 73.8 | MPa | ASTM D-790 |
| 断裂时之拉力伸张度 (+250℉(+122℃)) | >260 | % | ASTM D-638 |
| IZOD冲击强度 (+73℉) | 0.8 | ft.lb/in | ASTM D-256 |
| 扩散因数 (+73℉(+23℃)10Hz) | 0.005 | ASTM D-150 | |
| 弯曲疲劳忍耐限度 (+23℃) | 31.0 | MPa | ASTM D-671 |
| 绝缘强度 (Short Time,90 mils) | 490(125mils) | V/mil | ASTM D-149 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 电阻系数 (+73℉(+23℃)0.2%HO) | 5×10 | ohm-cm | ASTM D-257 |
| 电弧抵抗力 (120mil(3.1mm)) | 168no tracking | Sec. | ASTM D-495 |
| 绝缘系数 (+73°F(+23℃)10to10Hz) | 3.9 | ASTM D-150 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 (-40 to +85℉) | 2.0-4.5 | 10-5in/in.°F | ASTM D-696 |
| 热变形温度 | ASTM D-648 | ||
| (0.5MPa) | 174 | ℃ | |
| (66psi) | 345 | ℉ | |
| 熔点 | 175 | ℃ | ASTM D-2133 |
| 热变形温度 (1.8MPa) | 158 | ℃ | ASTM D-648 |
| 可燃烧性 | 94HB | UL-94 | |
| 熔点 | 347 | ℉ | ASTM D-2133 |
| 热变形温度 (264psi) | 316 | ℉ | ASTM D-648 |
| 线性热膨胀系数 (-40 to +29℃) | 3.6-8.1 | 10-5m/m.℃ | ASTM D-696 |