东莞市铭汇塑胶有限公司
LG Chemical HIPS 405AF PS, Flame Retardant
Polymer,Thermoplastic,Polystyrene (PS),Polystyrene, Flame Retardant
LG Chemical
产品说明:
Description: Injection Molding, PS, Flame Retardant
Application: Electric Parts Requiring Flame Retardancy
CAS: 9003-55-8, 158725-44-1 and 1309-64-4
Information provided by LG Chemical
LG Chemical HIPS 405AF PS, Flame Retardant 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| 处理 | 0.010 | 0.010 | Injection Molding |
| 线性成型收缩率,Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| 熔体流动速率 | 15 g/10 min @Load 5.00 kg, Temperature 200 °C |
15 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 90 | 90 | ASTM D785 |
| 抗张强度(屈服) | 25.5 MPa @Thickness 3.20 mm |
3700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| 伸长率 (断裂) | 60 % @Thickness 3.20 mm |
60 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| 屈服伸长率 | >= 5.0 % @Thickness 3.20 mm |
>= 5.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| 弯曲强度 | 43.1 MPa @Thickness 3.20 mm |
6260 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| 弯曲模量 | 2.16 GPa @Thickness 3.20 mm |
313 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.392 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| 0.392 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
0.735 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 | |
| 0.785 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
1.47 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 | |
| 0.981 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.84 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 耐电弧性 | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | |
| 热丝引燃 (HWI) | 15 - 30 sec @Thickness >=1.50 mm |
15 - 30 sec @Thickness >=0.0591 in |
|
| 15 - 30 sec @Thickness >=2.50 mm |
15 - 30 sec @Thickness >=0.0984 in |
||
| 15 - 30 sec @Thickness >=3.00 mm |
15 - 30 sec @Thickness >=0.118 in |
||
| 高电弧燃烧指数(HAI) | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
|
| >= 120 arcs @Thickness 2.50 mm |
>= 120 arcs @Thickness 0.0984 in |
||
| >= 120 arcs @Thickness 3.00 mm |
>= 120 arcs @Thickness 0.118 in |
||
| 高压电弧跟踪率，HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 82.0 °C @Thickness 6.40 mm |
180 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 77.0 °C @Thickness 6.40 mm |
171 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| 维卡软化温度 | 83.0 °C @Load 5.00 kg |
181 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
| UL RTI | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=2.50 mm |
122 °F @Thickness >=0.0984 in |
||
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| UL RTI，机械冲击 | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=2.50 mm |
122 °F @Thickness >=0.0984 in |
||
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| UL RTI，机械无冲击 | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=2.50 mm |
122 °F @Thickness >=0.0984 in |
||
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| 可燃性(UL94) | V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
|
| V-0 @Thickness >=2.50 mm |
V-0 @Thickness >=0.0984 in |
||
| V-0 @Thickness >=3.00 mm |
V-0 @Thickness >=0.118 in |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| 料筒中部温度 | 190 - 200 °C | 374 - 392 °F | Injection Molding |
| 料筒前部温度 | 200 - 210 °C | 392 - 410 °F | Injection Molding |
| 射嘴温度 | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| 加工（熔体）温度 | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| 模具温度 | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| 干燥温度 | 60.0 - 70.0 °C | 140 - 158 °F | Injection Molding |
| 干燥时间 | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 背压 | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| 螺杆转速 | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |