DuPont Performance Polymers Zytel? HTN FR52G30NHF BK337 Polyphthalamide (PPA)

Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 30% Glass Fiber Reinforced

DuPont Performance Polymers

产品说明:

30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide with Improved Flow

Zytel HTNFR52G30NHF BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin with improved flow. It is also a PPA

Information provided by DuPont Performance Polymers

DuPont Performance Polymers Zytel? HTN FR52G30NHF BK337 Polyphthalamide (PPA) 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.46 g/cc	0.0527 lb/in3	DAM; ISO 1183
线性成型收缩率,Flow	0.0030 cm/cm	0.0030 in/in	DAM; ISO 294-4 2577
线性成型收缩率，横向	0.010 cm/cm	0.010 in/in	DAM; ISO 294-4 2577

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	135 MPa	19600 psi	50%RH; ISO 527-1/-2
	145 MPa	21000 psi	DAM; ISO 527-1/-2
伸长率 (断裂)	1.9 %	1.9 %	50%RH; ISO 527-1/-2
	2.1 %	2.1 %	DAM; ISO 527-1/-2
拉伸模量	10.7 GPa	1550 ksi	DAM; ISO 527-1/-2
	11.3 GPa	1640 ksi	50%RH; ISO 527-1/-2
弯曲强度	200 MPa	29000 psi	50%RH; ISO 178
	225 MPa	32600 psi	DAM; ISO 178
弯曲模量	9.80 GPa	1420 ksi	DAM; ISO 178
	10.8 GPa	1570 ksi	50%RH; ISO 178
简支梁无缺口冲击强度	4.00 J/cm2	19.0 ft-lb/in2	50%RH; ISO 179/1eU
	4.50 J/cm2	21.4 ft-lb/in2	DAM; ISO 179/1eU
	3.50 J/cm2 @Temperature -30.0 °C	16.7 ft-lb/in2 @Temperature -22.0 °F	50%RH; ISO 179/1eU
	4.00 J/cm2 @Temperature -30.0 °C	19.0 ft-lb/in2 @Temperature -22.0 °F	DAM; ISO 179/1eU
简支梁缺口冲击强度	0.700 J/cm2	3.33 ft-lb/in2	DAM; ISO 179/1eA
	0.700 J/cm2	3.33 ft-lb/in2	50%RH; ISO 179/1eA
	0.700 J/cm2 @Temperature -30.0 °C	3.33 ft-lb/in2 @Temperature -22.0 °F	DAM; ISO 179/1eA
	0.700 J/cm2 @Temperature -30.0 °C	3.33 ft-lb/in2 @Temperature -22.0 °F	50%RH; ISO 179/1eA

电气性能	额定值 (公制)	额定值 (英制)	测试方法
相比耐漏电起痕指数(CTI)	600 V	600 V	DAM; IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	18.0 μm/m-°C	10.0 μin/in-°F	DAM; ISO 11359-1/-2
	12.0 μm/m-°C @Temperature 55.0 - 160 °C	6.67 μin/in-°F @Temperature 131 - 320 °F	DAM; ISO 11359-1/-2
	18.0 μm/m-°C @Temperature -40.0 - 23.0 °C	10.0 μin/in-°F @Temperature -40.0 - 73.4 °F	DAM; ISO 11359-1/-2
线性热膨胀系数,横向流动	62.0 μm/m-°C	34.4 μin/in-°F	DAM; ISO 11359-1/-2
	60.0 μm/m-°C @Temperature -40.0 - 23.0 °C	33.3 μin/in-°F @Temperature -40.0 - 73.4 °F	DAM; ISO 11359-1/-2
	95.0 μm/m-°C @Temperature 55.0 - 160 °C	52.8 μin/in-°F @Temperature 131 - 320 °F	DAM; ISO 11359-1/-2
熔融温度	310 °C	590 °F	DAM; first heat; ISO 11357-1/-3
载荷下热变形温度(1.8 MPa)	281 °C	538 °F	DAM; ISO 75-1/-2
UL RTI	140 °C @Thickness 0.400 mm	284 °F @Thickness 0.0157 in	UL 746B
	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in	DAM; UL 746B
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in	DAM; UL 746B
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in	UL 746B
可燃性(UL94)	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	DAM; IEC 60695-11-10
	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in	DAM; IEC 60695-11-10
极限氧指数	37 %	37 %	DAM; ISO 4589-1/-2
灼热丝易燃指数	700 °C @Thickness 0.400 mm	1290 °F @Thickness 0.0157 in	DAM; IEC 60695-2-1/2
	775 °C @Thickness 3.00 mm	1430 °F @Thickness 0.118 in	DAM; IEC 60695-2-1/3
	960 °C @Thickness 0.400 mm	1760 °F @Thickness 0.0157 in	DAM; IEC 60695-2-1/2
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	DAM; IEC 60695-2-1/2

材料描述		测试方法
Additives	Release agent
Delivery Form	Pellets
部件标识代码	>PA6T/66-GF30FR<	ISO 11469
	>PPA-GF30FR<	SAE J1344
加工	Injection Moulding
供货地区	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
UL recognition	UL	DAM