PA66 Zytel 70G35HSLRA4 BK267

35% Glass Reinforced, Heat Stabilized, Hydrolysis Resistant, Polyamide 66

Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in3	DAM; ISO 1183
Melt Density	1.27 g/cc @Temperature >=260 °C	0.0459 lb/in3 @Temperature >=500 °F
Water Absorption	5.5 % @Thickness 2.00 mm	5.5 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	1.70 % @Thickness 2.00 mm	1.70 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Number	125 cm3/g	1.25 dl/g	DAM; ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	DAM; ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	DAM; ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	140 MPa	20300 psi	50% RH; ISO 527-1/-2
	210 MPa	30500 psi	DAM; ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	DAM; ISO 527-1/-2
	5.0 %	5.0 %	50% RH; ISO 527-1/-2
Tensile Modulus	8.00 GPa	1160 ksi	50% RH; ISO 527-1/-2
	11.0 GPa	1600 ksi	DAM; ISO 527-1/-2

PA66 Zytel 70G35HSLRA4 BK267

尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，尼龙6为聚己内酰胺，而尼龙66为聚己二酸己二胺，尼龙66比尼龙6要硬l2%；其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙1010、尼龙46、尼龙7、尼龙9、尼龙13，新品种有尼龙6I、尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙、单体浇铸尼龙（MC尼龙）、反应注射成型(RIM)尼龙、芳香族尼龙、透明尼龙、高抗冲（超韧）尼龙、电镀尼龙、导电尼龙、阻燃尼龙，尼龙与其他聚合物共混物和合金等，满足不同特殊要求，广泛用作金属，木材等传统材料代用品。

特性

　　尼龙作为大用量的工程塑料，广泛用于机械、汽车、电器、纺织器材、化工设备、航空、冶金等领域。

　　成为各行业中不可缺少的结构材料，其主要特点如下：

　　1．优良的力学性能。尼龙的机械强度高，韧性好。

　　2．自润性、耐摩擦性好。尼龙具有很好的自润划性，摩擦系数小，从而，作为传动部件其使用寿命长。

　　3.优良的耐热性。如尼龙46等高结晶性尼龙的热变形温度很高，可在150℃下长期期使用。PA66经过

　　玻璃纤维增强以后，其热变形温度达到250℃以上。

　　4.优异的电绝缘性能。尼龙的体积电阻很高，耐击穿电压高，是优良的电气、电器绝缘材料。

　　5.优良的耐气候性。

　　6.吸水性。尼龙吸水性大，饱和吸水可达到3%以上。在一定程度影响制件的尺寸稳定性。

应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等

PA66 Zytel 70G35HSLRA4 BK267 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！