| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 9.0 | g/10min | |
| 吸水率 | ASTM D-570 | 0.22 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.41 | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 80 | Mscal | |
| 拉伸长率 | ASTM D-638 | 65 | % | ||
| 拉伸强度 | ASTM D-638 | 640 | Kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 920 | Kg/cm2 | ||
| 弯曲弹性率 | ASTM D-790 | 26500 | Kg/cm2 | ||
| 摩擦系数 | ASTM D-1894 | 0.22 | |||
| IZOD缺口冲击强度 | ASTM D-256 | 7.0 | kg.cm/cm | ||
| 电气性能 | 表面电阻系数 | ASTM D-257 | 1×1016 | Ω.cm | |
| 介电损耗正切 | ASTM D-150 | 0.006 | |||
| 绝缘破坏电压 | ASTM D-149 | 19 | KV/mm | ||
| 耐ARC性 | ASTM D-495 | ＞200 | sec | ||
| 体积电阻系数 | ASTM D-257 | 1×1014 | Ω | ||
| 介电常数 | ASTM D-150 | 3.7 | |||
| 加工性能 | 成型收缩率 | ASTM D-955 | 2.0 | % | |
| 热性能 | 热变形温度 | 18.6 | ASTM D-648 | 110 | ℃ |
| 线膨胀系数 | ASTM D-696 | 11-13 | ×10-5cm/cm/℃ | ||
| 热变形温度 | 4.6 | 160 | Kg/cm2 | ||
| 熔点 | ASTM D-1525 | 166 | ℃ | ||
| 燃烧性 | UL 94 | HB | |||
POM(聚甲醛树脂)定义:聚甲醛是一种没有侧链、高密度、高结晶性的线型聚合物。按其分子链中化学结构的不同，可分为均聚甲醛和共聚甲醛两种。两者的重要区别是:均聚甲醛密度、结晶度、熔点都高，但热稳定性差，加工温度范围窄(约10℃)，对酸碱稳定性略低;而共聚甲醛密度、结晶度、熔点、强度都较低，但热稳定性好，不易分解，加工温度范围宽(约50℃)，对酸碱稳定性较好。是具有优异的综合性能的工程塑料。有良好的物理、机械和化学性能，尤其是有优异的耐摩擦性能。俗称赛钢或夺钢，为第三大通用工程塑料。 适于制作减磨耐磨零件，传动零件，以及化工，仪表等零件。
合成树脂中的一种，又名聚甲醛树脂、POM塑料、赛钢料等;是一种白色或黑色塑料颗粒，具有高硬度、高钢性、高耐磨的特性。主要用于齿轮，轴承，汽车零部件、机床、仪表内件等起骨架作用的产品。