| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 30 | g/10min | |
| 吸水率 | ASTM D-570 | >0.01 | % | ||
| 密度 | ASTM D-1505 | 0.91 | g/cm3 | ||
| 物理性能 | 模具收缩率 | KPIC Method | 1.4-1.8 | % | |
| 机械性能 | 拉伸强度（屈服） | ASTM D-638 | 300 | kgf/cm2 | |
| 弯曲模量 | ASTM D-790 | 16000 | kgf/cm2 | ||
| IZOD缺口冲击强度 | ASTM D-256 | 12 | kgf/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 98 | R Scale | ||
| 断裂伸长率 | ASTM D-638 | <200 | % | ||
| 电气性能 | 介电强度 | ASTM D-149 | 40 | KV/М | |
| 抗电弧径迹性 | ASTM D-495 | 130 | sec | ||
| 体积电阻率 | ASTM D-257 | 1 | 1017Ω.H | ||
| 损耗因数 | 1KHz | ASTM D-150 | 2 | 10-4 | |
| 介电常数 | 1KHz | ASTM D-150 | 2.3 | ||
| 热性能 | 热导率 | KPIC Method | 3 | 10-4calcm/cmsec℃ | |
| 维卡软化点 | ASTM D-1525 | 152 | ℃ | ||
| 比热 | KPIC Method | 0.46 | |||
| 热变形温度 | ASTM D-648 | 131 | ℃ | ||
| 热膨胀系数 | ASTM D-696 | 10 | |||